Tese de Doutorado
DOI
10.11606/T.85.2013.tde-29042013-095446
Documento
Autor
Nome completo
Amanda Abati Aguiar
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2013
Orientador
Banca examinadora
Braga, Francisco Jose Correa (Presidente)
Fernandes, Stela Maria de Carvalho
Ribeiro, Christiane
Rossi, Wagner de
Salvador, Vera Lucia Ribeiro
Título em português
Avaliação do recobrimento biomimétrico em compósitos de alumina-zircônia texturizadas superficialmente com laser de femtossegundo
Palavras-chave em português
alumina-zircônia
laser de femtossegundo
recobrimento biomimético
SBF
texturização superficial
Resumo em português
O principal objetivo deste trabalho foi estudar a influência do tratamento superficial com laser de femtossegundo em amostras de alumina e compósito de alumina-zircônia estabilizada com ítria para depósito e aderência de apatita. Os resultados obtidos mostraram que houve a formação de apatita sobre as superfícies das amostras que foram texturizadas com laser de femtossegundo e em seguida imersa em 1,5 SBF. Este método biomimético pôde, por conseguinte, tornar estas cerâmicas bioativas. Também houve a formação de apatita na superfície das amostras sem o tratamento a laser. Os efeitos da texturização na superfície para as diferentes cerâmicas e a influência do tempo de imersão em 1,5 SBF são discutidos, a fim de determinar a condição ótima para estimular a deposição e a adesão da apatita na superfície dos materiais. Finalmente, os resultados obtidos das diferentes análises são comparados. A adesão da hidroxiapatita é essencial para interação com o substrato e depende das propriedades das superfícies dos materiais. A qualidade desta adesão influenciará sua morfologia e a capacidade futura de osseointegração. As características de superfície dependem da química de superfície, energia de superfície e topografia de superfície. Geralmente, a reatividade de superfície e energia de superfície pode ser influenciada pelas características de molhabilidade, influenciando o desempenho de biomateriais. A adesão e crescimento da apatita depositada também é função da rugosidade superficial. O tratamento superficial com laser de femtossegundo melhora consideravelmente a adesão da apatita obtida pelo recobrimento biomimético nas superfícies dos materiais.
Título em inglês
Evaluation of biomimetic coating in zirconia-alumina composite textured surface with femtosecond laser
Palavras-chave em inglês
alumina-zirconia
biomimetic coating
femtosecond laser
SBF
surface texturing
Resumo em inglês
The main objective of this work was to study the influence of femtosecond laser surface treatment on samples of alumina and composite of zirconia-alumina yttria stabilized for deposit and adhesion of apatite. The results showed that there was apatite formation on the surfaces of the samples that have been textured with femtosecond laser and then immersed in SBF 1.5. This biomimetic method can therefore make these bioactive ceramics. There was also the formation of apatite in the samples without laser treatment. The effects of texturing surface for the different ceramics and the influence of immersion time in SBF 1.5 are discussed in order to determine the optimal conditions to promote the deposition and the adhesion of the apatite in the material`s surface. Finally, the results of the different analyzes are compared. The adhesion of hydroxyapatite is essential for interaction with the substrate and depends on the properties of material´s surface. The quality of this adhesion will influence their morphology and the future ability of osseointegration. The surface characteristics depend on the surface chemical, surface energy and surface topography. Generally, the reactivity of surface and the energy of surface can be affected by wetting characteristics influencing the performance of biomaterials. The adhesion and growth of apatite deposited is also a function of surface roughness. The femtosecond laser surface treatment greatly improves the adhesion of apatite obtained by biomimetic coating on the surfaces of materials.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-06-06
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.