Master's Dissertation
DOI
Document
Author
Full name
Michele Cristina Biondo de Castro
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2018
Supervisor
Committee
Lima, Nelson Batista de (President)
Almeida, Gisele Fabiane Costa
Massi, Marcos
Title in Portuguese
Efeito da nitretação por plasma no comportamento em fadiga da liga Ti-6Al-4V
Keywords in Portuguese
fadiga
liga de titânio Ti-6Al-4V
nitretação por plasma
Abstract in Portuguese
A liga Ti-6Al-4V apresenta excelentes propriedades mecânicas, baixa densidade, alta dureza e resistência à corrosão. Entretanto, tratamentos superficiais como a nitretação por plasma são amplamente utilizadas para melhorar a resistência a fadiga desta liga. O objetivo deste trabalho foi tratar termoquimicamente a liga Ti-6Al-4V por meio da nitretação por plasma a fim de verificar a sua influência nas propriedades de fadiga e comparar os resultados obtidos com as não nitretadas. Este tratamento superficial foi realizado com o objetivo de retardar a etapa de nucleação da trinca. A nitretação por plasma foi realizada em temperaturas em torno de 720°C por 4 horas, numa atmosfera de N2, Ar e H2 (5:5:1). Foi realizado um tratamento térmico nas amostras para se obter a microestrutura de Widmanstätten. A temperatura usada foi de 1050°C por 30 minutos. A caracterização microestrutural das amostras nitretadas e não nitretadas foi realizada usando difração de raios X (DRX), microscopia óptica (MO), e microscopia eletrônica de varredura (MEV). Os resultados da difração de raios X das amostras nitretadas mostram a presença de fases: α, β, ε-Ti2N, e δ-TiN e nas amostras não nitretadas as fases α e β. Essas análises revelaram a presença de uma superfície rica em nitretos seguida de uma zona de difusão com nitrogênio na matriz. A rugosidade superficial foi estudada, e foi observada um aumento na rugosidade de 61% após a nitretação. Os testes de fadiga foram realizados em uma máquina de ensaios flexo rotativa, com uma razão de carregamento R=-1 . Os resultados obtidos mostraram que as propriedades de fadiga foram melhoradas após a nitretação por plasma, retardando a etapa de nucleação de trinca.
Title in English
Nitriding plasma effect on Ti-6Al-4V fatigue behavior
Keywords in English
fatigue
plasma nitriding
Ti-6Al-4V alloy
Abstract in English
The Ti-6Al-4V alloy presents excellent mechanical properties, low density, high toughness and corrosion resistance. However, surface treatments like plasma nitriding are widely used to improve the fatigue resistance of this alloy. Therefore, the aim of this work was to treat thermochemically Ti-6Al-4V alloy by means of plasma nitriding to verify its influence in fatigue properties and compare the results with the untreated ones. This surface treatment was performed with the purpose of retards the crack initiation. The plasma nitriding was performed in temperatures around 720°C for 4 hours, with a gas atmosphere N2, Ar and H2 (5:5:1). A heat treatment was made in the samples to obtain a Widmanstätten microstructure. The temperature used was 1050°C for 30 minutes. Microstructural characterizations of nitrided and non-nitrided samples were carried out using X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). The XRD results of the nitrided sample showed the presence of the α, β, ε-Ti2N, and δ-TiN phases. These analyses revealed a surface layer rich in nitrides on the surface, followed by a diffusion layer of nitrogen in the matrix. The surface roughness was compared between the nitrided and non-nitrided layer, and it was observed that the roughness increased 61% after the plasma nitriding. Fatigue tests were performed in a rotating bending testing machine with a stress ratio (R=-1). The results obtained in fatigue tests showed that the fatigue properties were improved after plasma nitriding, retarding the crack initiation.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
2018CastroEfeito.pdf (3.52 Mbytes)
Publishing Date
2019-05-08
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.