Thèse de Doctorat
DOI
10.11606/T.85.2007.tde-29032012-141245
Document
Auteur
Nom complet
Daniela de Fatima Teixeira da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Ribeiro, Martha Simões (Président)
Braga Junior, Roberto Alves
Line, Sergio Roberto Peres
Souza, Eunezio Antonio de
Zezell, Denise Maria
Titre en portugais
Caracterização e modelagem dos fenômenos anisotrópicos do colágeno após irradiação com Laser polarizado de emissão vermelha
Mots-clés en portugais
birrefringência
colágeno
geração de segundo harmônico
laser
microscopia de polarização
óptica não-linear
Resumé en portugais
O colágeno é a forma funcional de um oligômero biológico, cujos monômeros são aminoácidos quirais. Tecidos ricos em colágeno são estruturas opticamente anisotrópicas, birrefringentes e não-lineares. O objetivo deste trabalho foi caracterizar o colágeno tipo I não irradiado e após irradiação com laser de He-Ne polarizado, utilizando a microscopia de polarização para investigação da birrefringência, e a geração de segundo harmônico (GSH) para análise da susceptibilidade não-linear. Doze ratos Wistar foram divididos em quatro grupos, de acordo com as idades: 34, 48, 62 e 76 dias. Os grupos receberam, respectivamente, 1; 5; 9 e 13 irradiações de D= 1J/cm2, durante 46s, no tendão de Aquiles que, aleatoriamente, foi escolhido ser o direito ou esquerdo. Os animais foram então sacrificados e os tendões extraídos para a preparação das amostras. Para a microscopia de polarização foram obtidos cortes com 8μm de espessura, e as birrefringências de forma e intrínseca foram avaliadas. Para a GSH foi utilizado um laser de Ti:Safira (150fs) com 76MHz de taxa de repetição, diâmetro do feixe φ= 40μm, comprimento de onda central λ= 800nm e Δλ= 10nm e Pp= 110mW. Um polarizador linear foi posicionado no caminho do feixe. Duas objetivas foram utilizadas para focalizar e coletar a radiação incidente e emergente da amostra, respectivamente. Um analisador, também linear, foi introduzido logo após a objetiva coletora. Um filtro absorvedor na faixa infravermelha do espectro eletromagnético, mas transmissor na faixa azul, foi utilizado para garantir que apenas λ= 400nm era medido. A razão, ρ, entre dois tensores de hiperpolarizabilidade independentes foi estudada. As amostras irradiadas apresentaram maior birrefringência (Δn) e maior susceptibilidade não-linear (ρ), em comparação com as não irradiadas. Estes resultados indicam que o laser de He-Ne polarizado alinha as fibrilas de colágeno ao longo eixo do tendão.
Titre en anglais
Caracterization and modelling of collagen anisotropical phenomenons after irradiation with red emission polarized Laser
Mots-clés en anglais
anisotropy
birefringence
collagen
helium-neon lasers
laser radiation
polarization
skin
Resumé en anglais
The collagen is the functional form of a biological oligomer whose monomers are chiral amino acids. Tissues filled up of collagen are anisotropic optically structures, birefringent and nonlinear. The purpose of this study was characterizing nonirradiated and polarized He-Ne laser irradiated type I collagen using polarized light microscopy to investigate the birefringence and the second harmonic generation (SHG) to analyze the nonlinear susceptibility. Twelve Wistar rats were alienated into four groups according to the ages: 34, 48, 62 and 76 days. The groups received, respectively, 1; 5; 9; and 13 irradiations of D= 1J/cm2 during 46s on Achilles tendon, which was chosen randomly as right or left. Thereafter, the animals were sacrificed and the tendons were extracted to prepare the specimens. For polarized light microscopy, eight-μm sections were obtained to evaluate the form and intrinsic birefringences. For SHG, it was used a Ti:Safira (150fs) laser at a repetition rate of 76MHz, beam diameter of φ= 40μm, wavelength of λ= 800nm and Δλ= 10nm and Pp= 110mW. The beam passed through a linear polarizer and two microscope objectives were used to focalize and collect the incident and emergent radiation, respectively. A second linear polarizer was placed after of collecting objective. An infrared absorber and blue transmitter filter was used a sure that only λ= 400nm was measured. The ratio, ρ, between two hyperpolarizability tensors was studied. The irradiated samples presented higher birefringence (Δn) and nonlinear susceptibility (ρ) when compared to nonirradiated samples. These results indicate that a polarized He-Ne laser aligns the collagen fibrils to the long tendon axis.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-04-04
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.