Mémoire de Maîtrise
DOI
10.11606/D.85.2019.tde-29012019-143023
Document
Auteur
Nom complet
Fernando dos Santos Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Yamagata, Chieko (Président)
Castanho, Sonia Regina Homem de Mello
Setz, Luiz Fernando Grespan
Titre en portugais
Estudo de síntese de silicato de lantânio tipo apatita pelo método sol-gel seguido de precipitação de Na2SiO3
Mots-clés en portugais
apatita
IT-SOFC
silicato de lantânio
síntese
sol-gel
Resumé en portugais
Cerâmicas de silicato de lantânio tipo apatita têm sido estudadas devido ao grande interesse tecnológico para aplicação como eletrólito em células a combustível de óxido sólido de temperatura intermediária (IT-SOFC: Intermediate Temperature Solid Oxide Fuel Cell). A condutividade iônica dessas cerâmicas em temperaturas intermediárias (600-800°C) é maior do que a da YSZ (Ytria Stabilized Zirconia) utilizada como eletrólito em SOFCs de alta temperatura (800-1000°C). Neste trabalho, silicato de lantânio tipo apatita foi sintetizado pelo método sol-gel seguido de precipitação, a partir de Na2SiO3 como fonte de sílica. No método proposto, estudou-se rotas de síntese em meio ácido e básico para a formação do gel de sílica, seguida de precipitação. A fase cristalina de silicato de lantânio tipo apatita foi obtida pela calcinação de pós sintetizados a 900°C. Esta temperatura é muito inferior às praticadas em outros métodos convencionais de síntese. As análises por difração de raios X (DRX) mostraram silicato de lantânio tipo apatita como fase principal do material sintetizado na rota de síntese em pH ácido. No entanto, uma fase secundária indesejável, La2Si2O7, foi identificada quando o pó cerâmico foi calcinado a 1200°C. Por outro lado, pela rota básica, fase única de silicato de lantânio tipo apatita foi obtida após tratamento térmico dos precursores a 900 e 1200°C. Pastilha cerâmica obtida a partir dos pós obtidos e sinterizados a 1400°C por 4h, apresentaram fase cristalina pura de silicato de lantânio tipo apatita. Microscopia eletrônica de varredura (MEV) foi utilizada para observar a morfologia dos pós e microestrutura das pastilhas sinterizadas. Pós cerâmicos finos com tamanho de partículas submicrométricas e microestrutura típica de apatita foram alcançadas pelo método proposto.
Titre en anglais
Synthesis study of lanthanum silicate apatite type by sol-gel method followed by precipitation from Na2SiO3
Mots-clés en anglais
apatite
IT-SOFC
lanthanum silicate
sol-gel
synthesis
Resumé en anglais
Lanthanum silicate apatite-type ceramics have been studied because of the great technological interest for IT-SOFC applications as electrolyte (Intermediate Temperature Solid Oxide Fuel Cell). Ionic conductivity of those ceramics at intermediate temperatures (600-800°C) is higher than that of YSZ (Ytria Stabilized Zirconia) electrolyte used at high-temperatures (800-1000 °C) SOFCs. In this work, lanthanum silicate apatite-type was synthesized by sol-gel method followed by precipitation from Na2SiO3 as a source of silica. In the proposed method, synthesis routes in acid and basic medium to the formation of silica gel, followed by precipitation were studied. Apatite crystalline phase of lanthanum silicate ceramic was obtained by calcining the powders at 900°C. This temperature is much lower than those other conventional methods of synthesis. Analysis by x-ray diffraction (XRD) showed the lanthanum silicate apatite-type phase as the main phase of the synthesized material at the pH acid synthesis route. However, undesirable secondary phase, La2Si2O7, was recognized when the powder was calcined at 1200°C. On the other hand, by the basic route, single apatite-type phase powder was obtained after thermal treatment of the precursors at 900 and 1200°C. Ceramic pellet obtained from those powders sintered at 1400°C for 4h, presented pure apatite crystalline phase of lanthanum silicate. Scanning electron microscopy (SEM) was used to observe morphology of powders and microstructure of sintered pellets. Sub micrometric size powders and apatite typical microstructure ceramic were reached by the suggested method.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
2016SilvaEstudo.pdf (1.59 Mbytes)
Date de Publication
2019-02-08
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.