Disertación de Maestría
DOI
10.11606/D.85.2015.tde-28082015-103250
Documento
Autor
Nombre completo
Arthur Maximo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Rossi, Wagner de (Presidente)
Berretta, José Roberto
Riva, Rudimar
Título en portugués
Comparação entre soldagem de chapas finas de tântalo e monel 400 com laser pulsado de Nd:YAG e com laser contínuo de fibra
Palabras clave en portugués
chapas finas
corrosão
Monel
soldagem a laser
Tântalo
Resumen en portugués
Neste trabalho foram realizados experimentos de soldagem de chapas de Tântalo e Monel 400 com 100 m de espessura. Foram realizadas soldas em um laser de Nd:YAG operando em modo pulsado e em um Laser de Fibra operando em modo contínuo. Em seguida a microestrutura das amostras foram analisadas através de microscopia ótica e foram realizados ensaio de microdureza Vickers. As amostras que apresentaram melhores resultados foram submetidas a ensaios de tração e a ensaios de corrosão. Após análise dos resultados observou-se que a soldagem a laser apresenta muitos benefícios em relação a outros processos convencionais para chapas finas. A soldagem no modo pulsado apresentou maior relação de aspecto se comparado a soldagem em modo contínuo. A soldagem em modo contínuo apresentou uma velocidade de soldagem muito superior ao modo pulsado. Os resultados indicaram que a soldagem no modo pulsado apresenta maior aplicabilidade para chapas finas, devido à necessidade um controle preciso sobre a intensidade aplicada.
Título en inglés
Comparison between welding of thin sheets of Tantalum and Monel 400 with pulsed Nd:YAG laser and continuous fiber laser
Palabras clave en inglés
corrosion
laser welding
Monel
tantalum
thin sheets
Resumen en inglés
This work carried out welding experiments of Tantalum and Monel 400 plates with 100 mm thickness. Welds were made with an Nd: YAG laser operating in a pulsed mode and in a fiber laser operating in continuous mode. Then the microstructure of the samples were analyzed by optical microscopy and were performed Vickers microhardness test. Samples that showed better results were subjected to tensile tests and the corrosion tests. After analysis of the results showed that the laser welding offers many benefits over other conventional processes for thin sheets. The welding in pulsed mode presented in superior aspect ratio compared to welding in continuous mode. The welding in continuous mode showed a much higher welding speed to pulsed mode. The results indicated that the welding in pulsed mode shows more applicability for sheet metal, due the need of a precise control of applied intensity.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-08-31
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.