Tesis Doctoral
DOI
10.11606/T.85.2015.tde-25052015-085428
Documento
Autor
Nombre completo
Heloísa Augusto Zen
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Lugão, Ademar Benévolo (Presidente)
Nunes, Regina Célia Reis
Perez, Giovanni Gonzales
Ribeiro, Geise
Scuracchio, Carlos Henrique
Título en portugués
Desenvolvimento de elastômeros fluorados multifuncionais baseados em nanocompósitos
Palabras clave en portugués
enxertia induzida por radiação
fluoroelastômero
nanocompósito
Resumen en portugués
Os polímeros fluorados são conhecidos por suas ótimas propriedades mecânicas, pela alta estabilidade térmica e pela resistência a ambientes químicos agressivos, e por causa destas propriedades são muito utilizados em indústrias automobilística, petroquímica, de manufatura, dentre outras. Para aprimorar as propriedades térmicas e de barreira a gases da matriz polimérica, é muito utilizado a incorporação de nanopartículas nesta matriz, pois após a incorporação o nanocompósito permanece com suas próprias características e adquire novas propriedades devido a presença da nanopartícula. Devido as características dos fluoropolímeros, sua modificação estrutural e morfológica é muito difícil de ser obtida por técnicas tradicionais e para transpor essa dificuldade a radiação ionizante é uma técnica muito utilizada e eficaz para a alteração estrutural de polímeros fluorados. Neste trabalho foram desenvolvidos nanocompósitos poliméricos à base de fluoroelastômero (FKM) incorporado com quatro diferentes nanopartículas: argila Cloisite 15A, POSS 1159, POSS 1160 e POSS 1163. Após obtenção dos filmes de nanocompósitos foi realizado o processo de enxertia de estireno induzida por radiação ionizante, seguida de sulfonação para obtenção de membrana trocadora de íons. O efeito da incorporação de nanopartículas e da radiação ionizante nos filmes desenvolvidos foram caracterizados por difração de raios X, análise térmica, análise mecânica, microcospia eletrônica de varredura e intumescimento; enquanto que as membranas obtidas foram avaliadas quanto ao grau de enxertia, capacidade de troca iônica e intumescimento. Após a caracterização os filmes, foi verificado que a reticulação foi o efeito predominante nos nanocompósitos irradiados antes da vulcanização, enquanto que a degradação foi o efeito predominante nos nanocompósitos irradiados após a vulcanização.
Título en inglés
Development of multifunctional fluoroelastomers based on nanocomposites
Palabras clave en inglés
fluoroelastomer
nanocomposite
radiation grafiting
Resumen en inglés
The fluoropolymers are known for their great mechanical properties, high thermal stability and resistance to aggressive chemical environment, and because of those properties they are widely used in industries, such as automobile, petroleum, chemistry, manufacturing, among others. To improve the thermal properties and gases barrier of the polymeric matrix, the incorporation of nanoparticle is used, this process permits the polymer to maintain their own characteristics and acquire new properties of nanoparticle. Because of those properties, the structural and morphological modification of fluoropolymers are very hard to be obtained through traditional techniques, in order to surmount this difficulty, the ionizing radiation is a well-known and effective method to modify fluoropolymers structures. In this thesis a nanocomposite polymeric based on fluoroelastomer (FKM) was developed and incorporated with four different configurations of nanoparticles: clay Cloisite 15A, POSS 1159, POSS 1160 and POSS 1163. After the nanocomposites films were obtained, a radiation induced grafting process was carried out, followed by sulfonation in order to obtain a ionic exchanged membrane. The effect of nanoparticle incorporation and the ionizing radiation onto films were characterized by X-ray diffraction, thermal and mechanical analysis, scanning electron microscopy and swelling; and the membranes were evaluated by degree of grafting, ionic exchange capacity and swelling. After the films were characterized, the crosslinking effect was observed to be predominant for the nanocomposites irradiated before the vulcanization, whereas the degradation was the predominant effect in the nanocomposites irradiated after vulcanization.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-06-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.