Tesis Doctoral
DOI
https://doi.org/10.11606/T.85.2016.tde-23092020-093433
Documento
Autor
Nombre completo
Narayanna Marques Ferreira Mendes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Takiishi, Hidetoshi (Presidente)
Rossi, Jesualdo Luiz
Saeki, Margarida Juri
Schneider, Sandra Giacomin
Wendhausen, Paulo Antônio Pereira
Título en portugués
Obtenção e caracterização de ligas à base de Ti-Nb-Zr-(Ta) processadas por metalurgia do pó para aplicação como biomaterial
Palabras clave en portugués
ligas de titânio
metalurgia do pó
tratamento térmico
Resumen en portugués
Ligas quaternárias de titânio do sistema Ti-Nb-Ta-Zr são aplicadas como biomaterial devido à baixa massa específica, alta resistência ao desgaste, elevada resistência à corrosão, alta rigidez, baixo módulo de elasticidade e alta biocompatibilidade. O objetivo deste estudo foi analisar a atuação do tântalo como elemento estabilizador da fase β na formação de novas ligas quaternárias de Ti-Nb-Ta-Zr utilizando como base, a composição da liga ternária Ti-13Nb-13Zr, avaliando sua influência nas transformações microestruturais, mudanças de fases, microdureza e resistência à corrosão. Foram obtidas, ligas nas seguintes formulações, Ti-(13-x)Nb-(x)Ta-13Zr e Ti-13Nb-(13-y)Zr-(y)Ta com x, y = 1,5 - 3 - 4,5 e 6 % em massa. Os pós de partida (Ti, Nb e Zr) foram obtidos pelo método de hidrogenação e homogeneizados com Ta-cp em moinho planetário de alta energia. As amostras foram compactadas em matriz cilíndrica uniaxial seguidas de compactação isostática à frio, depois, sinterizadas com temperatura de 1150 °C / 10 h em vácuo e diferentes condições de resfriamento. As amostras foram caracterizadas por microscopia eletrônica de varredura, massa específica, técnica de difração de raios X, microdureza Vickers e ensaio eletroquímico de corrosão. A liga quaternária que produziu melhor resultado comparado a liga ternária foi a composição com 6 % em massa de tântalo, Ti-13Nb-6Ta-7Zr, com microestrutura composta de uma matriz de fase β e regiões de fase α com grãos equiaxiais e estruturas Widmanstätten, 96 % da densidade teórica, 347 HV de microdureza e densidade de corrente 2 x 10-11 A cm-2.
Título en inglés
Obtention and characterization of the alloys-based Ti-Nb-Zr-(Ta)
Palabras clave en inglés
heat treatment
powder metallurgy
titanium alloys
Resumen en inglés
Quaternary titanium alloys of Ti-Nb-Zr-Ta system are applied as biomaterial due low density, high strength wear, good corrosion resistance, high stiffness, low Young's modulus and high biocompatibility. The aim the present research was study tantalum effect as β stabilising elements to formation new quaternary Ti-Nb-Zr-Ta alloys based on the Ti-13Nb-13Zr alloy, evaluating the influence the microstructure transformations, phase changes, microhardness and corrosion resistance. Ti-(13-x)Nb-xTa-13Zr and Ti-13Nb-(13-y)Zr-(y)Ta alloys, where x, y = 1.5 - 3 - 4.5 and 6 %wt were produced. The starting powders (Ti, Nb and Zr) were obtained by hydrogenation method and homogenized with metallic tantalum high-energy planetary milling. Samples were produced by uniaxial and cold isostatic pressing with consolidation by sintering at 1150 °C for 10 hours under high vacuum under and different condition coolling. Sintered samples were characterized for SEM-EDS, density by Archimedes method, XRD, microhardness Vickers and potentiodynamic measurements. The quaternary alloy with better result compared to ternary alloy was the composition 6 %wt-Ta, Ti-13Nb-6Ta-7Zr. The microstructure of alloy consists of β-phase matrix and α-phase region of two structures: equiaxed and needle-like grains, known as Widmanstätten, with values of 96 % theoretical density, 347 HV, current density 2 x 10-11 A cm-2.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2016MendesObtencao.pdf (13.61 Mbytes)
Fecha de Publicación
2020-09-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.