Thèse de Doctorat
DOI
10.11606/T.85.2013.tde-22082013-141437
Document
Auteur
Nom complet
Fernando Rodrigues da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2013
Directeur
Jury
Baldochi, Sonia Licia (Président)
Carvalho, Jesiel Freitas
Mazzocchi, Vera Lucia
Morato, Spero Penha
Santo, Ana Maria do Espirito
Titre en portugais
Crescimento de fibras de molibdato duplo de lítio e lantânio e adaptação de sistema de alto vácuo para micro pulling-down
Mots-clés en portugais
fibras
fluoretos
micro pulling-down
molibdatos
Resumé en portugais
Neste trabalho, foi investigado o processo de crescimento de fibras monocristalinas (FMc) para aplicação em sistemas laser. Para o aperfeiçoamento na fabricação de FMc de fluoretos, foi projetada e construída uma nova câmara de crescimento para um forno comercial de micro-pulling down (μ-PD), permitindo um rígido controle da atmosfera de processamento, (sob vácuo, fluxo e atmosferas estáticas). Paralelamente, foi investigado o processo de crescimento de FMc de molibdatos duplos de terras raras, sendo crescidas e caracterizadas fibras puras e dopadas com Nd3+ do composto LiLa(MoO4)2 (LLM) com concentrações na faixa de 0,5 a 10mol%. A câmara de crescimento projetada para o controle de atmosfera foi avaliada em diversas condições de operação. Em particular, a mesma foi testada com o puxamento de fibras de LiF, sob atmosfera de CF4, para observação da sua eficiência no controle da atmosfera de crescimento. Foram obtidas FMc de LLM, homogêneas e transparentes; nas fibras puras foi observada a presença de facetas, entretanto, a adequação dos parâmetros de crescimento e a adição de dopantes permitiu a redução significativa destes defeitos. A difração de raios-x mostrou a cristalização no grupo espacial I41/a; medidas de tomografia por coerência ótica permitiram a detecção de centros de espalhamento em regiões onde ocorreram instabilidades no processo de crescimento. Foi possível observar que o coeficiente de segregação do íon Nd3+ é próximo à unidade nesta matriz. O ganho potencial para ação laser foi determinado utilizando-se uma solução numérica das equações de taxa do sistema em 805nm e regime CW. O ganho máximo da emissão laser em 1,064 μm foi previsto para a dopagem de 5% mol Nd3+.
Titre en anglais
Single crystal fibers growth of double lithium, lantanium molybdate and adjustment of a micro-pulling down furnace for high vacuum setup
Mots-clés en anglais
fibers
micro-pulling down
molybdate
Resumé en anglais
In this work we investigated crystal growth procedures aiming the development of single crystal fiber (SCF) for laser applications. For quality optimization in the fabrication of fluorides SCF a new growth chamber for a micro-pulling down furnace (μ-PD) was constructed targeting the fibers fabrication with strict atmosphere control (high vacuum, gas flux and static atmospheres). Simultaneously, the SCF growth process of rare earth double molybdates was studied. The growth of pure and Nd3+-doped SCF of LiLa(MoO4)2 (LLM) was studied in the range of 0,5 - 10mol% doping. The designed furnace growth chamber with controlled atmosphere was successfully constructed and tested under different conditions. Specially, it was tested with the growth of LiF SFC under CF4 atmosphere showing the expected results. Transparent and homogeneous SCF of Nd:LLM were grown. In the pure fibers was observed facets formation, however, these defects were minimized after tuning of the growth parameters and additionally with the fibers doping. X-ray analysis showed the crystallization of a single phase (space group I41/a); the optical coherence tomography showed the presence of scattering centers only in regions were some growth stability occurred due to the manual process control. The measured Nd3+ distribution showed uniform incorporation, indicative of a segregation coefficient close to unity in LLM. The potential laser gain of the system was determined using a numerical solution of the rate equations system for the 805nm, CW pumping regime, showing the maximum laser emission gain at 1.064 μm for a Nd3+-doping of 5mol%.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-08-28
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.