Tesis Doctoral
DOI
10.11606/T.85.2010.tde-20062011-152743
Documento
Autor
Nombre completo
Marcelo Marques Tusi
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Spinacé, Estevam Vitorio (Presidente)
Anaíssi, Fauze Jacó
Muccillo, Eliana Navarro dos Santos
Santos, Mauro Coelho dos
Suffredini, Hugo Barbosa
Título en portugués
Preparação de híbridos metal/carbono por carbonização hidrotérmica para aplicação na oxidação eletroquímica de metanol
Palabras clave en portugués
carbonização hidrotérmica
células a combustível
híbridos metal/carbono
oxidação do metanol
PtRu/C
Resumen en portugués
Neste trabalho foram preparados híbridos PtRu/Carbono e Ni/Carbono pelo método da carbonização hidrotérmica para aplicação na oxidação eletroquímica do metanol. Nesse processo, uma fonte de carbono e os sais metálicos, em meio aquoso, foram submetidos ao tratamento hidrotérmico a 200 ºC em uma autoclave. Na preparação dos híbridos PtRu/Carbono foram estudados o uso de diferentes agentes para ajuste do pH do meio reacional, a influência da adição de surfactante, a razão atômica Pt:Ru, a fonte de carbono, a carga metálica e o tempo de síntese. Para os híbridos Ni/Carbono estudaram-se parâmetros como a fonte de carbono e a adição de brometo de cetiltrimetilamônio. Os materiais obtidos foram caracterizados por espectroscopia de energia dispersiva de raios-X, difração de raios-X (DRX), microscopia eletrônica de transmissão, análise termogravimétrica, isotermas de B.E.T, espectroscopia no infravermelho com transformada de Fourier e voltametria cíclica. Os materiais foram testados para a oxidação eletroquímica do metanol voltametria cíclica, cronoamperometria e em células unitárias operando diretamente com metanol. Os híbridos PtRu/Carbono como-sintetisados não apresentaram atividade na oxidação do metanol. Após tratamento térmico a 900 oC, os materiais tornaram-se ativos e o melhor desempenho foi obtido para o material preparado utilizando celulose, hidróxido de tetrapropilamônio para ajuste do pH do meio reacional e carga metálica nominal de 5% em massa. Os resultados indicam que a atividade dos híbridos PtRu/Carbono, provavelmente, está relacionada à estrutura de poros, tamanho de partícula e presença de rutênio segregado. Os híbridos PtRu/Carbono foram tratados termicamente resultando em um material contendo carbono amorfo e grafítico. Os eletrocatalisadores PtRu/C preparados utilizando os híbridos Ni/Carbono como suporte mostraram-se mais ativos que os preparados utilizando o carbono comercial Vulcan XC72, considerado referência na área.
Título en inglés
Preparation of hibrids metal/carbon by hydrothermal carbonization for application in the electro-oxidation of methanol
Palabras clave en inglés
fuel cells
hibrids metal/carbon
hydrothermal carbonization
PtRu/C
Resumen en inglés
PtRu/Carbon and Ni/Carbon hybrid materials were prepared by hydrothermal carbonization process for application in the electro-oxidation of methanol. In this process, a carbon source and metal salts in aqueous solution were subjected to hydrothermal treatment at 200oC in an autoclave. In the preparation of hybrids PtRu/Carbon it was studied the use of different agents to adjust pH of the reaction medium, the influence of the addition of surfactant, the atomic ratio Pt: Ru, the source of carbon, the metallic charge and the synthesis time. For the hybrid Ni/Carbon it was studied parameters such as the carbon source and addition of cetyltrimethylammonium bromide. The obtained materials were characterized by energy dispersive X-ray, X-ray diffraction, transmission electron microscopy, thermogravimetric analysis, BET isotherms, Fourier transform infrared spectroscopy and cyclic voltammetry. The materials were tested for methanol electro-oxidation by cyclic voltammetry and chronoamperometry and in fuel cell operating directly with methanol. Hybrids PtRu/Carbon as-synthesized showed no activity for methanol electro-oxidation. After thermal treatment at 900oC, the materials become active and the best performance was obtained for the material prepared using cellulose as a carbon source, tetrapropylammonium hydroxide to adjust the pH of the reaction medium and nominal metal loading of 5 wt%. The results showed that the activity of the hybrids PtRu/Carbon appears to be related to pore volume, mesoporous structure, particle size and presence of segregated ruthenium. Hybrids Ni/Carbon heat-treated at 900oC resulted in a material containing amorphous and graphite carbon. The PtRu / C prepared using Ni / Carbon as support was more active than those prepared using commercial carbon Vulcan XC72, considered as a reference.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2010TusiPreparacao.pdf (13.34 Mbytes)
Fecha de Publicación
2011-06-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.