Mémoire de Maîtrise
DOI
10.11606/D.85.2011.tde-19122011-154824
Document
Auteur
Nom complet
José Antonio Batista de Souza
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2011
Directeur
Jury
Durazzo, Michelangelo (Président)
Carvalho, Elita Fontenele Urano de
Moreira, João Manoel Losada
Titre en portugais
Procedimento de fabricação de elementos combustível a base de dispersão com alta concentração de urânio
Mots-clés en portugais
combustível nuclear
dispersões
fabricação
placas combustíveis
U3O8-Al
U3Si2-Al
Resumé en portugais
O IPEN-CNEN/SP desenvolveu e disponibilizou para produção rotineira a tecnologia de fabricação de elementos combustíveis tipo dispersão, para uso em reatores nucleares de pesquisas. O combustível fabricado no IPEN-CNEN/SP está limitado à concentração de urânio de 3,0gU/cm3, para dispersões a base de U3Si2-Al, e de 2,3gU/cm3, para dispersões a base de U3O8-Al. O aumento da concentração de urânio nas placas combustíveis possibilita aumentar a reatividade do núcleo do reator e a vida útil do combustível. É possível aumentar-se a concentração de urânio no combustível até o limite tecnológico de 4,8gU/cm3 para a dispersão U3Si2-Al, e de 3,2gU/cm3 para a dispersão U3O8-Al, as quais estão bem qualificadas ao redor do mundo. Este trabalho tem como objetivo desenvolver o processo de fabricação de ambos os combustíveis com alta concentração de urânio, redefinindo-se os procedimentos de fabricação atualmente adotados no Centro do Combustível Nuclear do IPEN-CNEN/SP. Com base nos resultados obtidos conclui-se que para atingir a concentração desejada devem ser feitas algumas alterações nos procedimentos já estabelecidos, tais como mudança no tamanho de partícula dos pós e mudança no processo de alimentação da matriz de compactação. Os estudos realizados mostraram que as placas combustíveis com alta concentração de urânio a base da dispersão U3Si2-Al com 4,8 gU/cm3 fabricadas atenderam às especificações vigentes. Contudo, apesar da subjetividade da análise, a aparência da microestrutura obtida no núcleo das placas combustíveis a base da dispersão U3O8-Al com 3,2 gU/cm3 não foi considerada satisfatória devido à aparência da distribuição de vazios. O novo procedimento de fabricação foi aplicado na produção de placas combustíveis de dispersão U3Si2-Al com 4,8 gU/cm3 com urânio enriquecido, as quais foram utilizadas na montagem do elemento combustível parcial IEA-228 para ser testado quanto ao desempenho sob irradiação no reator IEA-R1 do IPEN-CNEN/SP. Esses novos combustíveis têm potencial para serem utilizados no novo Reator Multipropósito Brasileiro RMB.
Titre en anglais
Fabrication procedures for manufacturing high uranium concentration dispersion fuel elements
Mots-clés en anglais
dispersions
fuel plates
nuclear fuel
nuclear fuel manufacturing
U3O8-Al
U3Si2-Al
Resumé en anglais
IPEN-CNEN/SP developed the technology to produce the dispersion type fuel elements for research reactors and made it available for routine production. Today, the fuel produced in IPEN-CNEN/SP is limited to the uranium concentration of 3.0 gU/cm3 for U3Si2-Al dispersion-based and 2.3 gU/cm3 for U3O8-Al dispersion. The increase of uranium concentration in fuel plates enables the reactivity of the reactor core reactivity to be higher and extends the fuel life. Concerning technology, it is possible to increase the uranium concentration in the fuel meat up to the limit of 4.8 gU/cm3 in U3Si2-Al dispersion and 3.2 gU/cm3 U3O8-Al dispersion. These dispersions are well qualified worldwide. This work aims to develop the manufacturing process of both fuel meats with high uranium concentrations, by redefining the manufacturing procedures currently adopted in the Nuclear Fuel Center of IPEN-CNEN/SP. Based on the results, it was concluded that to achieve the desired concentration, it is necessary to make some changes in the established procedures, such as in the particle size of the fuel powder and in the feeding process inside the matrix, before briquette pressing. These studies have also shown that the fuel plates, with a high concentration of U3Si2-Al, met the used specifications. On the other hand, the appearance of the microstructure obtained from U3O8-Al dispersion fuel plates with 3.2 gU/cm3 showed to be unsatisfactory, due to the considerably significant porosity observed. The developed fabrication procedure was applied to U3Si2 production at 4.8 gU/cm3, with enriched uranium. The produced plates were used to assemble the fuel element IEA-228, which was irradiated in order to check its performance in the IEA-R1 reactor at IPEN-CNEN/SP. These new fuels have potential to be used in the new Brazilian Multipurpose Reactor - RMB.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-01-30
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.