Tesis Doctoral
DOI
https://doi.org/10.11606/T.85.2008.tde-18082009-181559
Documento
Autor
Nombre completo
Éverson do Prado Banczek
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Costa, Isolda (Presidente)
Melo, Hercilio Gomes de
Ramanathan, Lalgudi Venkataraman
Rodrigues, Paulo Rogerio Pinto
Wolynec, Stephan
Título en portugués
Desenvolvimento e caracterização de camadas de fosfato de zinco/níquel e zinco/nióbio
Palabras clave en portugués
Fosfatização
Fosfato de zinco
nióbio
Níquel
passivador
Resumen en portugués
Neste trabalho foi estudada a viabilidade de substituição do níquel presente em banhos de fosfato de zinco para a fosfatização do aço carbono (SAE 1010) por niobatos, ou oxalato de nióbio e amônio (Ox) e benzotriazol (BTAH). A substituição do passivador das camadas de fosfato obtidas, baseado em cromo hexavalente, por um banho passivador contendo Ox, também foi avaliada. Os resultados do presente trabalho mostraram que os compostos de nióbio podem substituir o níquel em banhos de fosfatização com várias vantagens, pricipalmente ambientais. Camadas com melhores propriedades foram obtidas com os banhos em presença de compostos de nióbio, pois um aumento da massa de fosfato depositada com menor tempo de imersão foi observado para estes banhos. Maior resistência à corrosão e maior eficiência de proteção foram obtidas para os revestimentos de fosfato de zinco em presença de niobatos (PZn+Nb) e de oxalato de nióbio e amônio e de benzotriazol (PZn+Ox+BTAH), quando comparados a camada tradicional em presença de níquel (PZn+Ni). As melhores propriedades de proteção, obtidas para os revestimentos testados foram relacionadas à morfologia dos cristais, espessura das camadas e com a menor porosidade dos revestimentos em presença de compostos de nióbio e de benzotriazol. Os resultados obtidos com os passivadores mostraram que o selante à base de Ox pode substituir o constituído por CrO3, mas somente sob determinadas condições de aplicação, aumentando a proteção contra a corrosão do aço carbono promovida pela camada de PZn+Ni.
Título en inglés
DEVELOPMENT AND CHARACTERIZATION OF ZINC/NICKEL AND ZINC/NIOBIUM PHOSPHATE LAYERS
Palabras clave en inglés
Fosfatização
Fosfato de zinco
nióbio
Níquel
passivador
Resumen en inglés
In the present study, the viability of the substitution of nickel found in some phosphating baths by niobates or by ammonium and niobium oxalate (Ox) with benzotriazole (BTAH), was investigated. The possible substitution of chromium hexavalent as passivating agent by Ox, was also evaluated. The results showed that the niobium compounds might replace the nickel from phosphating baths with many advantages, mainly due to the non toxic properties of these compounds. The phosphate layers obtained in the baths with niobium compounds presented better properties comparatively to that obtained in the nickel containing bath used as reference. The phosphate layers mass obtained in the baths with niobium compounds was superior to that deposited in the nickel containing ones, and were obtained at lower phosphating periods. Increased corrosion resistance and better protection efficiency were associated to the phosphate layers obtained in the baths with niobates (PZn+Nb) or niobium and ammonium oxalate with benzotriazole (PZn+Ox+BTAH), comparatively to that produced in the bath with nickel (PZn+Ni). The better protection properties of the phosphate layers obtained in the niobium compounds and benzotriazole containing solutions were related to the morphology of the deposited crystals, the phosphate layer thickness and the porosity of these layers. The results also showed that the Ox tested can be used as a sealing compound for phosphate layers and might replace the passivating CrO3, with the advantage of being ambientally friendly, resulting in increased corrosion resistance of the phosphate layer obtained in the solution with nickel (PZn+Ni).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-09-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.