• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Master's Dissertation
DOI
10.11606/D.85.2013.tde-17032014-153045
Document
Author
Full name
Natalia Torres Ratão
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Lugão, Ademar Benévolo (President)
Valera, Ticiane Sanches
Wiebeck, Helio
Title in Portuguese
Graxa de poliuréia - estudo da compatibilidade da poliuréia, polialfaolefina e politetrafluoretileno irradiado para melhoria da lubricidade e estabilidade
Keywords in Portuguese
graxa
lubrificante
polialfaolefina (PAO)
politetrafluoretileno (PTFE)
poliuréia (PUR)
radiação ionizante
Abstract in Portuguese
Lubrificantes são produtos gasosos, líquidos, semi sólidos ou sólidos (pó) que formam um filme entre duas partes evitando o atrito. Lubrificantes de alto desempenho são designados para trabalharem em condições severas de temperatura, pressão e contaminação. Os mais utilizados são os líquidos (óleos) e semi sólidos (graxas). As graxas são aplicadas aonde o óleo pode escorrer e em pontos de difícil acesso e são divididas basicamente em duas classes, sabão e não sabão. A graxa não sabão mais utilizada é a poliuréia, obtida pela reação entre aminas e isocianato, possui elevada tixotropia, alta rigidez dielétrica e excelente poder anticorrosivo, por isso é amplamente utilizada para lubrificação de motores elétricos e maquinário naval. Para obter uma graxa com altíssimo desempenho, nesse estudo foi utilizado o fluido lubrificante sintético polialfaolefina e também foi empregado o aditivo lubrificante sólido politetrafluoroetileno (PTFE) por apresentar o menor coeficiente de atrito conhecido, é comercialmente encontrado irradiado em ar para obter partículas menores e produzir grupos terminais oxigenados que são mais compatíveis com a superfície metálica. Os ensaios foram realizados de forma comparativa usando a graxa de poliuréia pura e aditivada com PTFE. As caracterizações foram feitas por espectroscopia de infravermelho, análise elementar de C, N, e H e índice de NCO livre, comprovando a formação de poliuréia de quatro carbonos (tetrauréia). As propriedades funcionais de ponto de gota e separação de óleo mostraram alta compatibilidade e estabilidade entre os polímeros, que aumentaram quando foi adicionado PTFE. A excelente resistência da graxa de tetrauréia pura ao desgaste e extrema pressão foram demonstradas pelo teste de quatro esferas e teste prático em rolamentos, caracterizando esta graxa como de alto desempenho quando comparada com as graxas mais utilizadas no mercado.
Title in English
Development of high performance lubricant through the compatibility of polyalphaolefin, polyurea and irradiated polytetrafluoroethylene
Keywords in English
grease
ionizing radiation
lubricant
polyalphaolefin (PAO)
polytetrafluoroethylene (PTFE)
polyurea (PUR)
Abstract in English
Lubricants are gaseous, liquid, semi solid or solid (powder) materials those form a film between two parties preventing friction. High performance lubricants are designed to work under severe conditions of temperature, pressure, and contamination. The most used are liquids (oils) and semi solids (greases). Greases are applied where oils can drain or in inaccessible places and are divided generally into two classes, soap and no soap. The most used non soap grease is polyurea, obtained by the reaction between amine and isocyanate, has highly thixotropic, high dielectric strength and excellent anticorrosive property, so it is widely used for lubrication of electric motors and shipbuilding machinery. For a grease with high performance, in this study was used a synthetic lubricant fluid, polyalphaolefin, and was also employed solid lubricant additive polytetrafluoroethylene (PTFE) due its lowest coefficient of friction, is found commercially irradiated in air to obtain smaller particles and to produce oxygenated terminal groups those are more compatible with the metal surface. The tests conducted were comparatively between pure polyurea grease and with PTFE additive. The characterizations were made by infrared spectroscopy and elemental analysis of C, N and H and Free NCO index, proving the formation of four carbons polyurea (tetraurea). The functional analysis of drop point and oil separation showed high stability and compatibility between the polymers increased when PTFE was added. The excellent resistance of pure tetraurea grease to wear and extreme pressure were demonstrated by four-ball and practical bearings tests, characterizing this grease as a high performance lubricant, when compared to most used greases in the market.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
2013RataoGraxa.pdf (2.32 Mbytes)
Publishing Date
2014-04-07
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.