Disertación de Maestría
DOI
10.11606/D.85.2010.tde-16012013-093254
Documento
Autor
Nombre completo
Gonçalo Siqueira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Rossi, Jesualdo Luiz (Presidente)
Politano, Rodolfo
Vatavuk, Jan
Título en portugués
Caracterização microestrutural, mecânica e tratamento térmico da liga AA-6082 obtida pelo processo de conformação por spray
Palabras clave en portugués
conformação por spray
dureza
liga de alumínio AA-6082
solubilização
tratamento térmico
Resumen en portugués
O processo de conformação por spray é interessante devido à capacidade de conjugar, em apenas uma etapa do processo, a vantagem da técnica de solidificação rápida combinada com alta produtividade dos processos de fundição convencional. Este processo permite a obtenção de materiais livre de macrossegregações, livre de porosidades e com microestrutura refinada. A evolução recente das pesquisas está levando ao desenvolvimento de novas ligas e os resultados têm sido interessantes. O processo de solidificação rápida inerente da conformação por spray permite a produção de ligas com composições diferentes das obtidas pela fundição convencional. O objetivo deste trabalho foi o de caracterizar mecanicamente uma liga de alumínio AA-6082 conformada por spray. Os resultados de testes de dureza Vickers são apresentados para seções de um preformado em relação a sua altura (em um arranjo tridimensional). O material foi avaliado na condição como conformado por spray e após tratamento térmico de solubilização a 525 ºC por 1 h, seguido por envelhecimento a 125 ºC por períodos distintos de 1 h, 10 h, 100 h e 500 h. É mostrado que o a liga AA 6082 conformada por spray mostra uma boa estabilidade térmica em relação a variação da dureza durante o envelhecimento.
Título en inglés
Microstructural characterization, mechanical and heat treatment of the spray formed AA60-82 alloy
Palabras clave en inglés
AA 6082 aluminum alloy
hardness
heat treatment
solution
spray forming
Resumen en inglés
The spray forming technology combines in a single step the advantages of the rapid solidification techniques and high the productivity of the conventional casting processes, allowing obtention of preforms with a refined microstructure, almost without porosity and macrosegregation free. The development and research efforts are leading to interesting alloys and materials production. The rapid solidification processes inherent to the spray forming allow the production of alloys with different compositions from those obtained by conventional ingot processes. The aim of this work was to carry out mechanical properties characterization of a spray formed AA-6082 alloy. The hardness results are presented in different sections related to the height of the spray formed preform (in a three-dimensional arrangement). The material was evaluated in the as sprayed condition and after heat treatment of solution at 525 ºC for 1 h, and aging for 1 h, 10 h, 100 h and 500 h periods. It was shown that the spray formed AA-6082 aluminum alloy is very stable regarding hardness variation during aging.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-02-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.