Thèse de Doctorat
DOI
10.11606/T.85.2005.tde-13032006-112231
Document
Auteur
Nom complet
Ana Maria do Espirito Santo
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Baldochi, Sonia Licia (Président)
Andreeta, Jose Pedro
Carvalho, Jesiel Freitas
Gomes, Laércio
Morato, Spero Penha
Titre en portugais
CRESCIMENTO E CARACTERIZAÇÃO DE FIBRAS MONOCRISTALINAS DE FLUORETOS DO TIPO LiY1-xTRxF4 (TR = TERRAS-RARAS)
Mots-clés en portugais
crescimento de cristais
fibras cristalinas
fluoretos
matrizes laser ativas
micro-pulling-down
monocristais
Resumé en portugais
Neste trabalho, foram estudados os processos de crescimento e caracterização de fibras monocristalinas de LiF e de LiYF4 (YLF) puras e dopadas com érbio (Er) ou neodímio (Nd) para aplicações ópticas. O crescimento destas fibras foi efetuado pelo método de micro-pulling-down (µ-PD) e o uso desta técnica é inédito para a obtenção de fibras monocristalinas destes fluoretos. Para tal finalidade, foi inicialmente construído no IPEN, um protótipo do sistema de µ-PD no modo resistivo para a compreensão dos parâmetros experimentais. Posteriormente, um equipamento comercial foi instalado e especialmente adaptado para o puxamento de fibras de fluoretos. Foram obtidas fibras monocristalinas de LiF, com boa qualidade óptica e estrutural e dimensões uniformes: diâmetros entre 0,5 e 1 mm e comprimentos de até 15 cm. A avaliação para o uso destas fibras como meio laser ativo indicou que suas propriedades ópticas são semelhantes às observadas em cristais volumétricos. Foi investigada a influência da geometria do capilar e cadinho, da atmosfera de crescimento e da composição de partida na estabilidade do processo de crescimento de fibras de YLF pelo método de µ-PD. Este material é muito sensível às contaminações procedentes da atmosfera de crescimento e a formação da fase estequiométrica, durante o crescimento da fibra, depende fortemente da atmosfera, da velocidade de puxamento e da composição de partida. Foram obtidas, de forma reprodutível, fibras puras com diâmetro uniforme (0,5 à 0,8 mm) e longo comprimento da fase estequiométrica (até 60 mm). Fibras de YLF com dopagens nominais de 10 mol% e 40 mol% de Er e com 1,7 mol% de Nd foram também obtidas com sucesso. As fibras de YLF:Er são homogêneas e livres de trincas, com distribuição regular de dopante e concentração próxima ao valor nominal. O perfil de distribuição de Nd na fibra de YLF:Nd é diferenciado. O valor do coeficiente de distribuição efetivo k foi estimado em 0,58; valor este superior aos valores encontrados para cristais volumétricos de YLF:Nd. A investigação das propriedades ópticas de absorção e emissão evidenciou características semelhantes às observadas em cristais volumétricos dopados com Nd, permitindo considerar as fibras de YLF:Nd com potencial para uso como meio laser ativo em dispositivos ópticos compactos com bombeamento por diodo.
Titre en anglais
GROWTH AND CHARACTERIZATION OF FLUORIDE CRYSTALLINE FIBRES TYPE LiY1-xTRxF4 (RE = RARE-EARTH)
Mots-clés en anglais
crystal fibers
crystal growth
fluorides
laser hosts
micro-pulling-down
single crystals
Resumé en anglais
In this work we present the growth and characterization of LiF and pure and rare-earth doped (Er and Nd) yttrium-lithium tetra-fluoride (LiYF4 or YLF) by the micro-pulling-down technique (µ-PD). The use of this technique is original for the present purpose. A m-PD prototype in the resistive mode was firstly built to understand the most important operational parameters. A commercial equipment was later installed and specifically modified to grow fluoride fibres. Regular and transparent single-crystalline fibres of LiF (diameter of 0.6 mm and length up to 150 mm) were obtained. LiF crystalline fibres as a potential laser media presented the same spectroscopic properties of bulk crystals. The influence of capillary and crucible shapes, growth atmosphere and start composition stoichiometry on the growth process of YLF fibers were also investigated. In general, the fluorides are very sensitive to moisture contamination. The growth atmosphere plays an important role on the stoichiometry deviation. Since this fluoride melts incongruently, any compositional changes inflences the solidification behavior of the material. Additionally, a limited pulling rate is required to the YLF phase formation and to the compositional homogeneity along the fiber. Homogeneous and regular section YLF fibres, with diametres between 0.5 to 0.8 mm and up to 60 mm in length, were obtained in a suitable and reproducible growth process. Er-doped (with nominal concentration of 10 and 40 mol%) and Nd-doped (with nominal concentration of 1.7 mol%) fibres were also successfully grown. Er-doped fibres were crack-free and the dopant concentration was practically uniform along the YLF phase. However, Nd–doped fibres presented a short initial transient in its concentration. The Nd distribution coefficient was evaluated as 0.58 for the YLF fibre. This value is greater than those estimated for YLF bulk crystals grown by normal freezing processes. The optical properties of the YLF:Nd fibres were similar to those observed in bulk crystals, which drive us to consider the YLF:Nd fibres as an important material to build compact all-solid-state lasers directly pumped by diodes.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Tese_AnaMaria.pdf (5.83 Mbytes)
Date de Publication
2006-09-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.