Mémoire de Maîtrise
DOI
10.11606/D.85.2018.tde-12092018-152418
Document
Auteur
Nom complet
Cristina Angioletto Pozenato
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Lugão, Ademar Benévolo (Président)
Fechine, Guilhermino José Macêdo
Rajagopal, Krishnaswamy
Titre en portugais
Efeitos da incorporação de nanotubos de carbono em elastômeros fluorados para auxílio em eventos de descompressão de CO2
Mots-clés en portugais
CO2
descompressão
elastômeros
nanotubos de carbono
Viton
Resumé en portugais
Diante da necessidade de produzir uma vedação com maior vida útil frente as condições de descompressão explosiva de CO2 incorporou-se quantidades diferentes de MWCNT (multiwalled carbono nanotubes) curtos e longos (0,25 phr e 1 phr) e com graus de funcionalidade de grupos oxigenados variando entre 0% e 7,5% em elastômeros fluorados. A incorporação foi realizada utilizando-se o processo de mistura em cilindro aberto (Copê) e as mantas de borracha obtidas foram termoprensadas e submetidas a doses de irradiação de 5, 10 e 20 kGy em ar atmosférico. Analisaram-se os nanocompósitos e os MWCNT por análises térmicas, difrações de raios-X e micrografias. A partir dos nanocompósitos também foram confeccionados corpos de prova para ensaios mecânicos, análises dinâmico-mecânicas, ensaios de dessorção. Os resultados indicaram em geral aumento dos módulos a 100% e secante a 15% nas amostras com adição de 1 phr, mas pouca mudança da temperatura de transição vítrea foi observada, indicando pouca alteração da mobilidade das cadeias. As micrografias apontaram algumas extremidades de MWCNT soltas da matriz polimérica após o processo de preparação da amostra. Os resultados apontaram melhora na dessorção dos nanocompósitos após a incorporação dos MWCNT.
Titre en anglais
Incorporation effects of carbon nanotube in fluorinated elastomers for assistance in CO2 explosive decompression
Mots-clés en anglais
carbon nanotubes
CO2
decompression
elastomers
Viton
Resumé en anglais
Faced with the need to produce a gasket with longer useful life against the explosive decompression conditions of CO2, it was incorporated different amounts of short and long MWCNT (0.25 phr and 1 phr) and degrees of oxygenated groups functionality ranging between 0% and 7.5% in fluorinated elastomers. The incorporation was performed using the open mill with two rolls (COPE) and rubber blankets were obtained thermopressed and subjected to radiation doses of 5, 10 and 20 kGy in air atmosphere. Nanocomposites and MWCNT were analyzed by thermal analysis, X-ray diffraction and SEM micrographs. From the nanocomposites were also prepared specimens for mechanical testing, dynamic mechanical analysis, desorption tests. The results indicated, in generally, an increase of modules to 100% and secant to 15% in the samples with the addition of 1 phr, however little change in the glass transition temperature was observed, indicating little variation of mobility of the chains. The micrographs showed some free ends of MWCNT the polymer matrix after sample preparation process. The results pointed improvement on dessorpotion of nanocomposites after the incorporation of MWCNT.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-09-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.