• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Odilon de Moraes Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2019
Director
Tribunal
Pillis, Marina Fuser (Presidente)
Antunes, Renato Altobelli
Xavier, Marcos Domingos
Título en portugués
Caracterização de um aço baixo carbono microligado ao vanádio utilizado na fabricação de componentes mecânicos
Palabras clave en portugués
aço microligado
aços HSLA
Charpy
resistência à tração
vanádio
Resumen en portugués
Os aços microligados representam, cada vez mais, uma parcela significativa de produção das usinas siderúrgicas para aplicações nos mais variados segmentos industriais tais como o automotivo, petróleo e gás, construção civil e agronegócio. A característica principal desses aços é a sua elevada resistência mecânica, aliada à boa tenacidade, ductilidade e soldabilidade; o que vem sendo obtido pela utilização de composições químicas específicas com teores baixos de carbono e de microligantes que conferem essas características a esses aços. Os microligantes utilizados são os mais variados, mas principalmente destaca-se a utilização do vanádio, nióbio, titânio, cobre, manganês, cromo, alumínio e nitrogênio. No presente trabalho foram estudadas as propriedades mecânicas de um aço microligado ao vanádio com 0,25%V e um aço AISI 1020. O aço microligado apresentou LRT, LE, alongamento e estricção de, respectivamente, 735,29 MPa, 559,07 MPa, 22,7% e 63,29%. O aço AISI 1020 apresentou, respectivamente, 437,42 MPa, 268,71MPa, 32,92% e 67,15%. O aço microligado apresentou propriedade mecânica superior à do aço AISI 1020 e ductilidade equivalente. Os resultados de impacto Charpy nas temperaturas de 23 °C, -20 °C e -40 °C foram, para o aço microligado, respectivamente de, 33,83 J, 12,41 J, e 6,54 J, e para aço AISI 1020 33,18 J, 5,07 J e 3,04 J, respectivamente. Observa-se tenacidade superior do aço microligado, quando comparado com o aço AISI 1020. O ensaio revelou microestruturas refinadas em ambos os aços, e tamanho de grão de 18μm n° 8 ASTM E 112 e de 25 μm n° 7 para o aço microligado e para o AISI 1020, respectivamente. Os testes eletroquímicos realizados em uma solução aquosa 3,5% em peso de NaCl revelaram que o aço microligado apresentou formação de camada passiva, e mostrou-se menos resistente à corrosão.
Título en inglés
Characterization of a low carbon vanadium microalloyed steel used in the manufacture of mechanical components
Palabras clave en inglés
Charpy
HSLA steels
microalloyed steel
tensile strength
vanadium
Resumen en inglés
Microalloyed steels are representing significant portion and increasingly steelmakers production and they are being applied to several industrial market segments such as automotive, oil and gas, civil construction and agribusiness. Its main characteristics are the superior tensile strength, toughness, ductility and good weldability. These properties are obtained through specific chemical compositions as low carbon and microalloying elements contents. Several microalloying elements can be used but some of them need to be mentioned such as vanadium, niobium, titanium, cooper, manganese, chromium, aluminum and nitrogen. In this work, the mechanical properties of a vanadium microalloyed and AISI 1020 steels were studied and compared. The microalloyed steel presented LRT, LE, elongation and toughness values of, respectively, 735.29 MPa, 559.07 MPa, 22.7% and 63,29%. AISI 1020 presented, respectively, 437.41 MPa, 268.70 MPa, 32.92% and 67.15%. The microalloyed steel presented mechanical properties superior to AISI 1020 and equivalent ductility. The results of the Charpy impact tests at the temperatures of 23 ° C, -20 ° C and -40 ° C were 33.83 J, 12.41 J, 6.54 J for the microalloyed steel, and for AISI 1020 steel the values were 33,18 J, 5.07 J and 3.04 J, respectively. The superior toughness of the microalloyed steel is observed when compared to the AISI 1020 steel. The metallographic examination showed fine grain microstructures ASTM E 112 No.8 and 7.for the microalloyed and for the AISI 1020, respectively. The electrochemical tests carried out in a 3.5 wt% NaCl aqueous solution showed that the microalloyed steel is less resistant to corrosion, and that a passive layer was formed on its surface.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-06-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.