Título en portugués
Síntese e caracterização de filmes nanocompósitos de TiO2/C para aplicações fotocatalíticas
Palabras clave en portugués
atividade fotocatalítica
carbono esfoliado
filmes de TiO2
heterojunção
TiO2/C
Resumen en portugués
O presente trabalho teve como objetivos a síntese, caracterização e avaliação do comportamento fotocatalítico de filmes de dióxido de titânio (TiO2) e filmes nanocompósitos heteroestruturados de TiO2/C. Os filmes foram obtidos pelo método sol-gel, depositados sobre substratos de vidro borossilicato, por meio da técnica de spray coating, e tratados termicamente em diferentes temperaturas. Grafite expandida, esfoliada em diferentes tempos pelo processo de esfoliação em fase líquida, foi utilizada como fonte de carbono. A descoloração do corante alaranjado de metila foi utilizada para investigar a atividade fotocatalítica dos filmes sob irradiação de luz ultravioleta e visível. A influência da temperatura de tratamento térmico, do teor de carbono e de agentes supressores na eficiência dos filmes também foi estudada. Todos os filmes exibiram a formação da fase anatase. A adição de carbono promoveu evidentes modificações morfológicas nos filmes híbridos que resultaram na melhora do seu desempenho. Os testes de remoção do corante indicaram que os filmes de TiO2 apresentam atividade fotocatalítica apenas sob radiação UV, com eficiência de 76,4 %. O filme híbrido de TiO2/10% de C, tratado termicamente a 450 ºC, exibiu o melhor comportamento fotocatalítico, com 79,5 % de remoção do corante sob luz visível. O mecanismo fotocatalítico dos filmes nanocompósitos foi proposto a partir dos resultados obtidos. A heterojunção TiO2/C formada apresenta um comportamento característico de heterojunções do tipo II. Tal efeito contribui para a ativação do fotocatalisador sob luz visível, o que favorece sua aplicação prática sob luz do Sol.
Título en inglés
Synthesis and characterization of nanocomposite TiO2/C films for photocatalytic applications
Palabras clave en inglés
exfoliated carbon
heterojunction
photocatalytic activity
TiO2 films
TiO2/C
Resumen en inglés
The present study aims the synthesis, characterization, and photocatalytic evaluation of the titanium dioxide (TiO2) films, and TiO2/C heterostructured nanocomposite films. The films were obtained by the sol-gel method, deposited on borosilicate glass substrates, using the spray coating technique, and heat treated at different temperatures. Expanded graphite was exfoliated at different times by the liquid phase exfoliation process and used as a carbon source. Methyl orange dye decolorization was used to investigate the photocatalytic activity of the films under UV and visible light irradiation. The influence of heat treatment temperature, carbon content, and the scavengers on the catalyst efficiency was also studied. All films exhibited the formation of the anatase phase. The addition of carbon promoted evident morphological changes in the hybrid films that resulted in an improvement in their performance. Dye removal tests indicated that the TiO2 films exhibited photocatalytic properties only under UV light with an efficiency of 76.4 %. The TiO2/10%-C hybrid film, heat treated at 450 ºC, exhibited the best photocatalytic behavior, with 79.5 % of dye removal under visible light. The photocatalytic mechanism of nanocomposite films was proposed based on the results obtained. The formed TiO2/C heterojunction shows a typical behavior of staggered gap heterojunctions. Such effect contributes to the photocatalyst activation under visible light, which favors its practical application under sunlight.
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2022-12-30