Disertación de Maestría
DOI
10.11606/D.85.2016.tde-04042016-140231
Documento
Autor
Nombre completo
Mariana Silva de Araujo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Genova, Luís Antonio (Presidente)
Castanho, Sonia Regina Homem de Mello
Ferreira, Eduardo Bellini
Título en portugués
Utilização de resíduos de catalisador (ECAT) e cinzas da casca de arroz (CCA) na elaboração de vidros silicatos soda-cal destinados a embalagem
Palabras clave en portugués
cinza da casca de arroz
resíduos de catalisador exaurido
resíduos sólidos industriais
vidros
vidros soda-cal
Resumen en portugués
Estudo realizado acerca da utilização de dois resíduos sólidos industriais (RSI) gerados em grande quantidade no Brasil, na obtenção de vidros soda-cal destinados à produção de embalagens. Os resíduos avaliados foram a cinza de casca de arroz (CCA) e resíduo do catalisador usado das unidades de Craqueamento Catalítico Fluido das Petroquímicas (ECAT), ambos podem ser classificados como resíduos sólidos de classe II de acordo com a norma NBR 10.004. Esta nova proposta para destinação desses resíduos é uma alternativa às atuais disposições, buscando não apenas minimizar os impactos ambientais gerados, mas também a valorização dos mesmos como matérias-primas. Para a produção das amostras, além da utilização dos RSIs, foram também utilizados óxidos fundente (Na2CO3) e estabilizante (CaO). Os resultados obtidos demonstraram que ambos podem ser usados como recebidos (sem tratamento prévio) substituindo matérias-primas importantes, fontes de Al2O3 e SiO2, necessárias para a formação de vidros. As amostras obtidas apresentaram a cor âmbar devido a presença de níquel (íons Ni2+) proveniente do ECAT e transmitância óptica de 18%. Estas, ainda demonstraram boa homogeneidade, i.e., ausência de bolhas e estriais e, resistências hidrolíticas média de 1,33x10-8 g/cm²·dia (superior à um vidro comercial de composição semelhante) de acordo com a ISO695-1984. O vidro obtido é adequado para aplicações que exigem baixa transmitância como embalagens de vidros em geral, os quais não requerem perfeita visibilidade e transparência. O teor de incorporação na composição final das amostras foi de aproximadamente 78% em massa.
Título en inglés
Use of rice rusk ash and spent catalyst as a source of raw material for the production and characterization of soda-lime silicate glasses destined for packaging
Palabras clave en inglés
glass
industrial solid waste
rice husk ash
soda-lime glass
spent catalyst
Resumen en inglés
In this study, the use of two industrial solid wastes (ISW), generated in large quantities in Brazil, were presented in production of soda-lime silicate glasses destined for packaging. The evaluated wastes were rice husk ash (RHA) and the spent catalyst at the Petrochemical Fluid Catalytic Cracking units (ECAT), both may be classified as a class II solid waste according to NBR 10.004. This new proposal for the allocation of such wastes is an alternative to current provisions, seeking not only to minimize environmental impacts, but also enrich them as raw materials. For the samples production, besides ISW were used melting oxide (Na2CO3) and stabilizer oxide (CaO).The results demonstrate that both can be used in their raw form (without treatment) replacing important raw materials, sources of Al2O3 and SiO2, essential for glass formation. The samples obtained presented amber color due to the presence of nickel (Ni²+ ion) from ECAT and 18% of optical transmittance. They also showed a good homogeneity, i.e., absence of bubbles and striae and 1,33x10-8 g/cm²·day of hydrolytic resistance according to ISO695-1984. Thus, the obtained glass is suitable for applications requiring low light transmittance such as colored glasses containers in general, which does not require perfect visibility and transparency. The incorporation in the final composition was approximately 78% in mass.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-04-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.