Tesis Doctoral
DOI
10.11606/T.85.2012.tde-03092012-143036
Documento
Autor
Nombre completo
Reinaldo Azevedo Vargas
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2012
Director
Tribunal
Seo, Emília Satoshi Miyamaru (Presidente)
Castanho, Sonia Regina Homem de Mello
Saeki, Margarida Juri
Toffoli, Samuel Marcio
Yoshimura, Humberto Naoyuki
Título en portugués
Síntese, processamento e caracterização de cátodo para aplicação em células a combustível de óxido sólido de temperatura intermediária
Palabras clave en portugués
cátodo
células a combustível
eletrólito
óxido sólido
técnica dos citratos
Resumen en portugués
Os filmes micrométricos contendo óxido misto de lantânio, estrôncio, cobalto e ferro (La0,60Sr0,40)(Co0,20Fe0,80)O3-δ - LSCF, misturado com (Ce0,90Gd0,10)O1,95 - CGO, são relevantes para a utilização como camada funcional para o cátodo da Célula a Combustível de Óxido Sólido de Temperaturas Intermediárias. Estes filmes foram depositados no um substrato cerâmico e denso de CGO ou CGO sobre (ZrO2)0.92(Y2O3)0.08 - YSZ. O estudo deste cátodo é fundamental, pois é nele que ocorre a reação de redução do gás oxigênio, e o seu desempenho eletroquímico depende da interface destes dois materiais. Neste sentido, o presente trabalho contribui para a síntese dos particulados de LSCF para o processamento de filmes, utilizando a técnica de deposição com uso de aerógrafo e para sua conformação em camadas contendo porosidade com espessuras entre 30 e 50 μm. Inicialmente, os particulados de LSCF foram sintetizados pela técnica do citratos e de LSCFCGO obtidos por mistura mecânica, sendo caracterizados por DRX para a confirmação da formação da estrutura cristalina ortorrômbica para o LSCF e cúbica para CGO. Em seguida, foram preparadas suspensões orgânicas de LSCF, LSCFCGO e CGO que foram alimentadas por gravidade em um aerógrafo manual para deposição sobre substrato do eletrólito. Para a conformação dos substratos de CGO ou YSZ, utilizou-se prensa uniaxial e isostática, sinterização e retificação. Verificaram-se, pelas micrografias, que os substratos CGO e YSZ apresentaram densidades (> 92%) suficientes para serem utilizados como eletrólitos. Os filmes de LSCF e LSCFCGO apresentaram-se com porosidades adequadas (> 30%) e espessura total de aproximadamente 40 μm, com boa aderência ao eletrólito. A presença do cátodo compósito contendo eletrólito de CGO sobre YSZ possibilitou aumento de 25% no desempenho eletroquímico (2,50 Ω.cm2 para 650ºC) em decorrência da melhora na reação de redução do oxigênio na interface cátodo/eletrólito.
Título en inglés
Synthesis, processing and characterization of cathode for application in intermediate temperature solid oxide fuel cells
Palabras clave en inglés
cathode
citrate technique
electrolyte
fuel cells
solid oxide
Resumen en inglés
The study of micrometrics films of (La0.60Sr0.40)(Co0.20Fe0.80)O3-δ - LSCF mixture with (Ce0.90Gd0.10)O1.95 - CGO is relevant for use as functional cathode of Intermediate Temperature Solid Oxide Fuel Cells (ITSOFC). These films were deposited on the CGO or CGO and YSZ dense ceramic substrate, used as electrolyte, structural component of the module. The study of this cathode is fundamental, because is there that occurs oxygen reduction reaction, and the electrochemical performance depends on the interface of these two materials. In this sense, this work contributes for the synthesis of LSCF particulates, for processing films using the wet powder spraying technique, adopted for the conformation of the ceramic films for allowing the attainment porous layers with thicknesses between 30 and 50 μm. Initially, the LSCF particulates were synthesized by the citrate technique and the LSCFCGO produced by solid mixture were characterized by XRD to confirm the formation of LSCF orthorhombic structure and CGO cubic structure. In the stage of formation were prepared organic suspensions of LSCF, LSCFCGO and CGO fed by gravity in a manual airbrush for electrolyte substrate deposition, sintering and grinding for thickness reduction. The micrographs showed that the CGO and YSZ substrates were dense (> 92%) enough to be used as solid electrolyte. The LSCF and LSCFCGO films presented with adequate porosity (> 30%) and total thickness of approximately 40 μm, with good adhesion to electrolyte. The presence of the composite cathode containing CGO or YSZ electrolyte allowed the increase of 25% in the electrochemical performance (2.50 Ω.cm2 to 650ºC) due to improvement in the oxygen reduction reaction at the interface cathode/electrolyte.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2012VargasSintese.pdf (8.40 Mbytes)
Fecha de Publicación
2012-11-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.