• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.85.2018.tde-01112018-153726
Documento
Autor
Nombre completo
Rodrigo Teixeira Bento
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Pillis, Marina Fuser (Presidente)
Antunes, Renato Altobelli
Bonturim, Everton
Título en portugués
Estudo da atividade fotocatalítica de filmes de TiO2 dopados com enxofre
Palabras clave en portugués
atividade fotocatalítica
dopagem com enxofre
filmes de TiO2
MOCVD
Resumen en portugués
O presente trabalho teve como objetivos o estudo das propriedades nanoestruturais, características morfológicas e avaliação do comportamento fotocatalítico de filmes de dióxido de titânio dopados com enxofre. Os filmes de TiO2 foram crescidos sobre borossilicato, por meio da técnica de MOCVD, na temperatura de 400 °C. O processo de dopagem com enxofre deu-se a partir do tratamento termoquímico de sulfetação, realizado sob atmosfera de H2 / 2%v. H2S, nas temperaturas de 50 °C, 100 °C e 150 °C, o que resultou em teores de S de 8 at.%, 3 at.% e 0,2 at.%, respectivamente. A degradação do corante alaranjado de metila foi utilizada para avaliar a atividade fotocatalítica dos filmes sob radiação ultravioleta e visível. Todos os filmes exibiram a formação da fase anatase, compostos por grãos bem definidos, e estrutura colunar densificada. Foi observada a formação de grupos SO42- na superfície dos filmes dopados, indicando a substituição dos íons Ti4+ pelo cátion S6+, e a formação da ligação Ti-O-S nos filmes. Os testes de degradação indicaram que os filmes de S-TiO2 apresentam atividade fotocatalítica tanto sob radiação UV, quanto em luz visível. O filme de 8 at.% S-TiO2, dopado a 50 °C, exibiu o melhor comportamento fotocatalítico, com 72,1 % de degradação do corante sob luz visível. Os resultados sugerem que a dopagem com S, além de formar uma morfologia favorável ao processo de fotocatálise, promoveu um deslocamento da absorção do TiO2 para a região do espectro visível, o que consequentemente permite a sua aplicação prática sob luz solar ou lâmpadas de luz visível.
Título en inglés
Study of photocatalytic activity of sulfur-doped TiO2 films
Palabras clave en inglés
MOCVD
photocatalytic activity
sulfur doping
TiO2 films
Resumen en inglés
The present work aims the study of the nanostructural properties, morphological characteristics and photocatalytic behavior evaluation of sulfur-doped titanium dioxide films. TiO2 films were grown on borosilicate by MOCVD at 400 °C. Sulfur doping process was carried out by the thermochemical treatment under H2 / 2%v. H2S atmosphere at 50 °C, 100 °C and 150 °C, which resulted in S contents of 8 at%, 3 at% and 0.2 at%, respectively. Methyl orange dye degradation was used to evaluate the photocatalytic activity of the films under UV-Vis radiation. All films exhibited the formation of the anatase phase, composed to well-defined grains, and dense columnar structure. SO42- groups were observed on the surface of all S-doped films, indicating the substitution of the Ti4+ ions by the S6+ cation, and the formation of Ti-O-S bond in the films. Degradation tests indicated that the S:TiO2 films present photocatalytic activity both under UV radiation and visible light. 8 at.% S:TiO2 film, doped at 50 °C, presented a higher photocatalytic performance, with 72.1 % of dye degradation under visible light. The results suggest that the sulfur doping, besides forming a morphology favorable to the photocatalysis process, caused a shift of the TiO2 films absorption to the visible spectrum region, which allows their practical application under sunlight or visible light bulbs.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2018BentoEstudo.pdf (4.52 Mbytes)
Fecha de Publicación
2018-11-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.