Thèse de Doctorat
DOI
https://doi.org/10.11606/T.85.2020.tde-01032021-103503
Document
Auteur
Nom complet
Isac Almeida da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2020
Directeur
Jury
Monteiro, Waldemar Alfredo (Président)
Batalha, Gilmar Ferreira
Marinucci, Gerson
Vatavuk, Jan
Titre en portugais
Mecanismos associados ao refino de grão em ligas de alumínio após processamento pela técnica de prensagem em canais equiangulares (PCE)
Mots-clés en portugais
deformação plástica intensa
liga de alumínio 1050
liga de alumínio 3003
prensagem em canais equiangulares
recristalização de não ferrosos
Resumé en portugais
A aplicação final dos materiais metálicos depende das propriedades físicas e mecânicas destes, que podem ser adquiridas por diversos mecanismos aos quais eles são submetidos. Uma propriedade que não raras vezes tem se tornado muito importante e decisiva na utilização dos metais é o tamanho médio de grão do material. Devido ao fato dos materiais metálicos com tamanho de grão muitíssimo pequeno, de ordem submicrométrica, ou nanométrica, apresentarem significativo aumento de resistência mecânica, a sua fabricação tem sido de interesse crescente. Entretanto, a prática industrial convencional para produzir apurado refinamento de grãos em materiais metálicos massivos é o processamento termomecânico, pelo qual, os menores tamanhos de grão obtidos são de ordem micrométrica, mas não submicrométrica ou a nanométrica. São apresentados neste trabalho os mecanismos associados ao refino de grão nas ligas de alumínio AA 1050 e AA 3003 após processamento pela técnica de Prensagem em Canais Equiangulares (PCE), que, por Deformação Plástica Intensa (DPI) bloqueará o movimento das discordâncias do material, conferindo-lhe alta resistência, boa tenacidade e grãos de tamanho nanométrico. Este bloqueio pode também ser obtido por encruamento, solução sólida e precipitação de solutos, porém, os métodos de refinamento de grãos em metais e ligas estão inseridos dentre os mais significativos avanços em metalurgia física.
Titre en anglais
Grain refining in aluminum alloys after processing by equal channel angular pressing techniques (ECAP) associated mechanisms
Mots-clés en anglais
aluminum alloy 1050
aluminum alloy 3003
intense plastic deformation
non-ferrous recrystallization
processing by equal channel angular pressing
Resumé en anglais
The final application of metallic materials depends on their physical and mechanical properties, which can be acquired by various mechanisms to which they are subjected. A property that has often become very important and decisive in the use of metals is the average grain size of the material. Due to the fact that metallic materials with a very small grain size, submicrometric, or nanometric, present a significant increase in mechanical resistance, their manufacture has been of increasing interest. However, the conventional industrial practice for producing refined grain refinement in massive metallic materials is thermomechanical processing, whereby the smallest grain sizes obtained are micrometric, but not submicrometric or nanometric. This research presents the mechanisms associated with grain refining in aluminum alloys AA 1050 and AA 3003 after processing by the Pressing Technique in Equiangular Channels (PCE), which, by Intense Plastic Deformation (DPI) will block the movement of material discrepancies, giving it high strength, good toughness and nanometer-sized grains. This blockage can also be obtained by hardening, solid solution and precipitation of solutes, however, the methods of grain refinement in metals and alloys are inserted among the most significant advances in physical metallurgy.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2021-03-02
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.