Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Cecilio Alvares da Cunha
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 1986
Directeur
Jury
Ramanathan, Lalgudi Venkataraman (Président)
Ambrozio Filho, Francisco
Goldenstein, Helio
Titre en portugais
Estudo da cinética da transformação de fase no estado sólido UAl3 + Al → UAl4
Mots-clés en portugais
cinética
ligas de alumínio
transformações de fase
Resumé en portugais
A cinética da transformação de fase UAl3 + Al → UAl4 foi estudada em duas ligas Al-U, com 31,4 % e 33,4 % U em peso respectivamente, através de metalografia quantitativa. Os resultados mostraram que esta transformação é um processo de nucleação e crescimento termicamente ativado, com a nucleação ocorrendo heterogeneamente nas interfaces UAl3/AI(∞) e o crescimento sendo controlado por difusão em volume. A energia de ativação empírica do processo foi determinada, cujo valor médio é da ordem de 54,8 kcal/mol. Foi verificado que a cinética de crescimento da fase UAl4 obedece uma lei parabólica. As interfaces UAl4/ UAl3 e UAl4/Al(∞) migram em direções opostas, sendo que a velocidade da interface UAl4/ UAl3 é aproximadamente cinco vezes maior que aquela da interface UAl4/Al(∞). O coeficiente de difusão química do Al e do U na fase UAl4 foi avaliado ser da ordem de 10-9 cm 2/s a 600°C.
Titre en anglais
Kinetics of solid state phase transformation UAl3 + Al → UAl4
Mots-clés en anglais
aluminium alloys
kinetics
phase transformations
Resumé en anglais
The kinetics of phase transformation UAl3 + Al → UAl4 of two Al-U alloys, with 31.4 and 33.4 wt % U respectively, was studied by quantitative microscopy. The results have shown that this transformation is a nucleation and thermally activated growth process. The nucleation occurs heterogeneously at the UAl3/AI(∞) interfaces and growth is controlled by volume diffusion. The empirical activation energy of the process was determined, whose mean value is of about 54.8 kcal/mol. It was verified that a parabolic growth law is obeyed. The UAl4/ UAl3 and UAl4/Al(∞) interfaces migrates in opposite directions, with the UAl4/ UAl3 interface velocity was approximately 5 times greater than that of UAl4/Al(∞) interface. The chemical diffusion coefficient of Al and U in the UAl4 phase were evaluated to be of the order of 10-9 cm 2/s at 600°C.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
1986CunhaEstudo.pdf (3.46 Mbytes)
Date de Publication
2012-11-09
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.