Disertación de Maestría
DOI
10.11606/D.85.2007.tde-24102011-105556
Documento
Autor
Nombre completo
Clovis Pinto
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Silva, Leonardo Gondim de Andrade e (Presidente)
Miranda, Leila Figueiredo de
Wiebeck, Helio
Título en portugués
Estudo do efeito da radiação ionizante sobre as propriedades da poliamida 6 com reforço de fibra de vidro
Palabras clave en portugués
efeitos de radiação
fibra de vidro
materiais reforçados
microscopia eletrônica de varredura
poliamidas
propriedades mecânicas
radiações ionizantes
Resumen en portugués
É cada vez maior a utilização de polímeros reforçados com fibra de vidro no mercado nacional. Entre eles utiliza-se a poliamida 6 que apresenta ótima resistência à tração, ao impacto e à absorção de umidade comparada à poliamida 6 sem reforço de fibra de vidro, sendo atualmente utilizada na indústria automobilística em peças sob o capô, em especial em carcaças de radiadores. Este trabalho foi realizado com o objetivo de estudar o efeito da radiação ionizante nas propriedades mecânicas (resistência à tração, à flexão e ao impacto Izod) e térmicas (resistência ao fio incandescente e temperatura de fusão) da poliamida 6 com reforço de fibra de vidro, submetida à diferentes doses de radiação (100 a 600 kGy). As amostras foram preparadas e irradiadas em um acelerador JOB 188 com feixe de elétrons de energia de 1,5 MeV em diferentes doses e uma taxa de dose de 22,61 kGy/h. Após a irradiação, as propriedades das amostras da poliamida 6 com reforço de fibra de vidro irradiada foram determinadas e comparadas com as amostras não irradiadas e constatou-se que as propriedades mecânicas de resistência à flexão e à tração aumentaram e a de resistência ao impacto diminuiu. Em relação à propriedade térmica de temperatura de fusão diminuiu de 224,4ºC para 212,5ºC mas a perda de massa diante do aumento constante da temperatura também diminuiu. Em relação à propriedade de resistência ao fio incandescente a poliamida 6 com reforço de fibra de vidro irradiada teve um bom desempenho. As imagens captadas por Microscopia Eletrônica de Varredura mostram que a irradiação provocou uma boa integração entre a fibra de vidro e o polímero o que foi responsável pelo bom desempenho na propriedade de resistência ao fio incandescente.
Título en inglés
Study of the effect of ionizing radiation on properties of polyamide 6 with fibreglass reinforcement
Palabras clave en inglés
fiber glass
ionizing radiations
mechanical properties
polyamides
radiation effects
reinforced materials
scanning electron microscopy
Resumen en inglés
It is each time more common the use of polymers reinforced with fibreglass in the domestic market. Between them it is used polyamide 6 that it presents good tension resistance, to the impact and the humidity absorption compared with non-reinforced, being also at the present time used in the automobile industry in parts underneath the hood, especially in the radiator frames. The aim of this work is to study the effect of ionizing radiation on properties of polyamide 6 with fibreglass reinforcement, undergone to different radiation doses. Samples were prepared and irradiated on JOB 188 accelerator with an electron beam energy of 1.5 MeV in air with different doses (100 to 600 kGy) and a dose rate of 22.61 kGy/h. Afterward the irradiation, the properties of the samples of irradiated polyamide 6 with fibreglass reinforcement were evaluated and compared with the samples non-irradiated. It evidenced that the mechanical properties flexural resistance and tension resistance increased and the resistance to the impact decreased. Regarding the thermal properties of the temperature of fusing decreased of 224,4ºC for 212,5ºC but the loss of mass ahead of the constant increase of the temperature also decreased. In the property of resistance to the glow wire the polyamide 6 with fibreglass reinforcement had a good performance. The images caught for Scanning Electronic Microscopy show that the irradiation provoked a good integration enters the fibreglass and polymer what was responsible for the good performance in the property of resistance to the glow wire.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
2007PintoEstudo.pdf (1.36 Mbytes)
Fecha de Publicación
2011-12-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.