Disertación de Maestría
DOI
10.11606/D.85.2013.tde-06062013-090450
Documento
Autor
Nombre completo
Eduardo Gurzoni Alvares Ferreira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Marumo, Júlio Takehiro (Presidente)
Gobbo, Luciano de Andrade
Vicente, Roberto
Título en portugués
Avaliação da alteração das propriedades da pasta de cimento em ambiente de repositório
Palabras clave en portugués
durabilidade
pasta de cimento
rejeitos radioativos
repositório
Resumen en portugués
Pasta de cimento é um material comum em repositórios para rejeitos radioativos, atuando como material estrutural e de imobilização. Sua utilização como material de preenchimento em um repositório tipo poço tubular profundo para fontes seladas, no entanto, requer um maior tempo de vida útil do material. O conhecimento de seu comportamento em longo prazo é necessário para garantir a segurança da instalação em milhares de anos. O presente trabalho avaliou as alterações na pasta de cimento induzidas por fatores de degradação, como ataque de agentes agressivos, alta temperatura e presença de campo de radiação. Corpos de prova (cps) de pasta de cimento foram submetidos a ensaios acelerados de degradação e os efeitos deletérios foram avaliados por meio de ensaios de resistência mecânica, variação dimensional, lixiviação/penetração de íons, DRX, TGA e MEV. Observou-se que a hidratação dos cps foi beneficiada pela imersão (em água destilada ou em solução salina) e alta temperatura, resultando em uma resistência maior. O armazenamento à seco prejudicou a hidratação, mantendo a resistência mais baixa. O tempo de imersão e a irradiação não foram capazes de alterar a mineralogia e a resistência da pasta de cimento.
Título en inglés
Assessment of cement paste properties changes in repository environment
Palabras clave en inglés
cement paste
durability
radioactive waste
repository
Resumen en inglés
Cement paste is widely used in repositories for radioactive wastes, acting as structural and immobilization material. However, its use as backfill material in boreholes for sealed sources requires a longer service life of this material. The assessment of the cement paste behavior in long term is needed to improve the confidence that the material will perform as required during the service life of the facility. This research evaluated the changes in cement paste induced by degradation parameters. Portland cement paste specimens (cps) were submitted to accelerated degradation tests and the damage effects was evaluated by mechanical strength, variation of sample mass and volume, leaching/penetration of ions, XRD, TGA and SEM. It was observed that cps hydration was benefited by immersion (in distilled water or salt solution) and high temperatures, resulting in a higher strength. Dry storage, however, influenced the hydration process and maintained strength lower. Time of treatment and irradiation were not able to alter mineralogy and durability of cement paste.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-07-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.