Master's Dissertation
DOI
10.11606/D.85.2013.tde-06062013-090450
Document
Author
Full name
Eduardo Gurzoni Alvares Ferreira
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Marumo, Júlio Takehiro (President)
Gobbo, Luciano de Andrade
Vicente, Roberto
Title in Portuguese
Avaliação da alteração das propriedades da pasta de cimento em ambiente de repositório
Keywords in Portuguese
durabilidade
pasta de cimento
rejeitos radioativos
repositório
Abstract in Portuguese
Pasta de cimento é um material comum em repositórios para rejeitos radioativos, atuando como material estrutural e de imobilização. Sua utilização como material de preenchimento em um repositório tipo poço tubular profundo para fontes seladas, no entanto, requer um maior tempo de vida útil do material. O conhecimento de seu comportamento em longo prazo é necessário para garantir a segurança da instalação em milhares de anos. O presente trabalho avaliou as alterações na pasta de cimento induzidas por fatores de degradação, como ataque de agentes agressivos, alta temperatura e presença de campo de radiação. Corpos de prova (cps) de pasta de cimento foram submetidos a ensaios acelerados de degradação e os efeitos deletérios foram avaliados por meio de ensaios de resistência mecânica, variação dimensional, lixiviação/penetração de íons, DRX, TGA e MEV. Observou-se que a hidratação dos cps foi beneficiada pela imersão (em água destilada ou em solução salina) e alta temperatura, resultando em uma resistência maior. O armazenamento à seco prejudicou a hidratação, mantendo a resistência mais baixa. O tempo de imersão e a irradiação não foram capazes de alterar a mineralogia e a resistência da pasta de cimento.
Title in English
Assessment of cement paste properties changes in repository environment
Keywords in English
cement paste
durability
radioactive waste
repository
Abstract in English
Cement paste is widely used in repositories for radioactive wastes, acting as structural and immobilization material. However, its use as backfill material in boreholes for sealed sources requires a longer service life of this material. The assessment of the cement paste behavior in long term is needed to improve the confidence that the material will perform as required during the service life of the facility. This research evaluated the changes in cement paste induced by degradation parameters. Portland cement paste specimens (cps) were submitted to accelerated degradation tests and the damage effects was evaluated by mechanical strength, variation of sample mass and volume, leaching/penetration of ions, XRD, TGA and SEM. It was observed that cps hydration was benefited by immersion (in distilled water or salt solution) and high temperatures, resulting in a higher strength. Dry storage, however, influenced the hydration process and maintained strength lower. Time of treatment and irradiation were not able to alter mineralogy and durability of cement paste.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2013-07-30
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.