Disertación de Maestría
DOI
https://doi.org/10.11606/D.82.2017.tde-17102017-114522
Documento
Autor
Nombre completo
Marisa de Cássia Registro Fonseca
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 1997
Director
Tribunal
Mazzer, Nilton (Presidente)
Barbieri, Cláudio Henrique
Chierice, Gilberto
Título en portugués
Ensaio mecânico de tração de uma poliuretana elastomérica derivada do óleo de mamona, para uso como implante tendinoso
Palabras clave en portugués
Elastômeros
Ensaios mecânicos
Implante tendinoso
Polímeros
Poliuretana derivada do óleo de mamona
Resumen en portugués
Com vistas ao seu emprego na confecção de implantes de tendões flexores para a mão, foi realizado um estudo in vitro das propriedades mecânicas da poliuretana elastomérica derivada do óleo da mamona. Corpos de prova, de formato e dimensões adequados ao estudo, estabelecidos pela norma ASTM 638, foram recortados de placas de poliuretana, obtidas pela polimerização de seus componentes básicos, o poliol Q 160 e o pré-polímero FN 329, na forma pura e associada a fios de poliéster longitudinalmente colocados no seu interior, dispostos paralelamente entre si, ou trançados, em número variando de um a sete, com incrementos de dois, segundo o grupo experimental. Os corpos de prova foram submetidos a ensaios de tração em máquina universal de ensaios, tendo sido analisados os parâmetros força de 1) resistência à ruptura, 2) tensão máxima, 3) deformação (alongamento), 4) resiliência e 5) módulo de elasticidade. Para cada grupo foram testados três corpos de prova e, dos valores obtidos para cada parâmetro individualmente, foi obtida uma média para execução da análise estatística. Os resultados mostraram que a associação da poliuretana com os fios de poliéster faz diminuir a capacidade de deformação da poliuretana pura, aumentando sua força de resistência, a tensão máxima, a resiliência e o módulo de elasticidade, propriedades cujos valores numéricos aumentam com o incremento do número e com o trançar dos fios, tendo sido muito significante com cinco e sete fios. Concluiu-se que, na forma associada, a poliuretana derivada do óleo da mamona constitui um material adequado para a confecção de implantes de tendão, passivos ou ativos.
Título en inglés
not available
Palabras clave en inglés
not availalbe
Resumen en inglés
With a view to using it to make flexor tendon implants for hand surgery, an in vitro study on the mechanical properties of the elastomeric poliurethane derived from castor oil was carried out. Dumb bell shaped specimens, of appropriate dimensions, as established by ASTM 638 standard, were cut out from poliurethane plaques, obtained by the polimerisation of its basic components, the Q 160 poliol and FN 329 prepolymer, either plain and combined with palallel or embroidered polyester threads, which varied from one to seven, at increments of two, according to the group. The specimens were submitted to traction in a universal testing machine and tested for the parameters 1) resistance to rupture, 2) maximal tension, 3) deformation (elongation), 4) resilience and 5) modulus of elasticity. Three specimens were tested per group and an average was calculated so as to allow for statistical analysis. The results showed that the combination with the polyester threads decreases the capacity of deformation of the polyurethane, at the same time that increases its resistance, maximal tension, resilience and modulus of elasticity, the values of these properties increasing in direct proportion to the number of threads, being higher for five and seven threads and for the embroidered threads. lts was concluded that when combined with the polyester threads, the polyurethane derived from castor oil is an adequate material to make either passive or active flexor tendon implants for hand surgery.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-10-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.