Disertación de Maestría
DOI
10.11606/D.76.2005.tde-31012006-162000
Documento
Autor
Nombre completo
José Ezequiel de Souza
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Hernandes, Antonio Carlos (Presidente)
Bianchi, Rodrigo Fernando
Nunes, Luiz Antonio de Oliveira
Título en portugués
Estudo das propriedades elétricas de vidros oxifluoroboratos de chumbo pela técnica de espectroscopia de impedância
Palabras clave en portugués
elétricas
impedância
oxifluoroboratos
propriedades
Resumen en portugués
A caracterização elétrica de materiais vítreos foi efetuada por meio da análise da condutividade em função da freqüência da amplitude do sinal (ac) e da condutividade dc, utilizando para tanto a técnica de espectroscopia de impedância (IS) e medidas da corrente elétrica direta em função da voltagem dc aplicada. As medidas de IS foram realizadas no intervalo de freqüência de 1 Hz até 1 MHz e em função da temperatura. Avaliou-se as propriedades elétricas de vidros oxifluoroboratos de chumbo (BPP), 50BO1.5 – (50-x)PbO – xPbF2, com x = 0, 5, 10, 15 e 20 (% catiônica). As amostras vítreas foram sintetizadas por mistura convencional e fusão das quantidades apropriadas dos reagentes. Observou-se que a condutividade dc aumenta com a temperatura seguindo a lei de Arrhenius, com uma única energia de ativação aparente para o processo de condução na matriz vítrea. Há também um aumento da condutividade em cinco ordens de grandeza, por uma relação “quase” linear, com o aumento do fluoreto de chumbo na composição das amostras. As técnicas de Calorimetria Exploratória Diferencial (DSC), Difração de Raios X (DRX), Microscopia Eletrônica de Varredura (MEV) e Espectrometria de Emissão Óptica com Plasma Acoplado Indutivamente (ICP-AES) foram empregadas para auxiliar no entendimento do sistema BPP e dos processos de condução envolvidos. A temperatura de transição vítrea e a densidade foram determinadas para todas as composições. As quantidades de boro e chumbo, determinadas pela técnica de ICP-AES, indicam uma perda de chumbo durante a preparação dos vidros, perda mais evidenciada para a composição de x = 20%. Com a aplicação de tensão dc sobre a amostra houve cristalização da fase β-PbF2 e redução para chumbo metálico.
Título en inglés
Electrical properties study of lead oxifluoroborates glasses by impedance spectroscopy technique
Palabras clave en inglés
electrical
impedance
oxifluoroborates
properties
Resumen en inglés
Electrical properties of lead oxifluoroborate glasses were investigated. Measurements were carried out by impedance spectroscopy (IS) in the frequency range from 1 Hz to 1 MHz and direct current (dc) measurements. All measurements were performed in a temperature between 25 and 300 °C. Glassy samples of 50BO1.5 – (50-x)PbO – xPbF2 system, where x = 0, 5, 10, 15 and 20 (cationic %), were synthesized by conventional mixing and melting of appropriate amounts of starting reagents. The glass conductivity increases with temperature following the Arrhenius law, with single apparent activation energy for conduction process. The lead fluoride addition even causes a conductivity enhancement which goes from 10-10 up to 10-4 S/cm at 250 °C. Differential Scanning Calorimetry (DSC), X-Ray Diffraction (DRX), Scanning Electron Microscopy (SEM) and Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES) techniques were applied to aid in the understanding of the material and its conductive processes. Glass transition temperatures and density were available for all compositions. Boron and lead amounts, determined by ICP-AES, are evidence of a process in which a lead is lost, a reason for density reduction of the x = 20% composition. The use of dc voltage caused a β-PbF2 phase crystallization and a lead reduction.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
disser_Ezequiel.pdf (3.07 Mbytes)
Fecha de Publicación
2006-02-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.