Disertación de Maestría
DOI
10.11606/D.76.2012.tde-17082012-110437
Documento
Autor
Nombre completo
Pedro Ivo Batistel Galiote Brossi Pelissari
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2012
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Guimarães, Francisco Eduardo Gontijo
Lisboa Filho, Paulo Noronha
Título en portugués
Síntese e caracterização de filmes finos SrTi1-xFexO3 nanoestruturados aplicados como sensor de gás ozônio
Palabras clave en portugués
Filmes finos
Nanoestrutura
Ozônio
Perovskita
Sensor de gás
Resumen en portugués
Neste trabalho, foram desenvolvidos filmes finos de composição SrTi1-xFexO3 (0,00≤ x ≤0,150) nanoestruturados visando sua aplicação como sensor de gás ozônio. Os filmes finos foram depositados através da técnica de deposição por feixe de elétrons (EBD) cujo alvo utilizado foram pastilhas obtidas a partir do pó cristalino SrTi1-xFexO3 (0,00≤ x ≤0,150) sintetizadas através do método dos precursores poliméricos. Foi observado a partir das analises termogravimétrica e térmica diferencial que a incorporação de ferro no sistema diminui a temperatura de queima do pó precursor, sugerindo que o ferro atua como catalisador na cadeia polimérica. Os filmes depositados por DFE apresentam-se no estado amorfo sendo necessário um tratamento térmico ex-situ para que a fase cristalina desejada seja obtida. Todos os filmes apresentaram uma boa aderência aos diferentes tipos de substratos utilizados. Após o processo de cristalização, os filmes depositados sobre diferentes substratos foram caracterizados através das técnicas de difração de raios-X, espectroscopia UV-Vis e microscopia de força atômica (MFA). Foi observado que um aumento na temperatura de tratamento térmico dos filmes leva a um aumento no grau de cristalização e a uma diminuição no valor da energia de gap, calculada a partir dos espectros UV-VIS. A analise por MFA mostrou que a mudança do tipo de substrato utilizado não influencia as propriedades estruturais e microestruturais dos filmes. Através da realização de medidas de resistência elétrica, observou-se que os filmes cristalinos submetidos a um tratamento térmico ex-situ a 500oC por 4 horas apresentaram uma boa sensibilidade ao gás ozônio sendo possível detectar a presença de até 75 ppb de ozônio.
Título en inglés
Synthesis and characterization of nanostructure SrTi1-xFexO3 thin films to be applied as ozone gas sensor
Palabras clave en inglés
Nanostructure
ozone
Ozone gas sensor
Perovskite
Thin films
Resumen en inglés
In this study, nanostructured thin films of SrTi1-xFexO3 (0.00 ≤ x ≤ 0.150) compositions were prepared looking their application as ozone gas sensor. The thin films were deposited using the technique of electron beam deposition (EBD) whose targets were obtained from polycrystalline SrTi1-xFexO3 (0.00 ≤ x ≤ 0.150) powders synthesized by the polymeric precursor method. It was observed from the thermogravimetric and differential thermal analysis that the incorporation of iron in the system decreases the calcination temperature of the precursor powders, suggesting that the iron acts as a catalyst in the polymer chain. The as obtained films deposited by EBD present an amorphous state being necessary a ex-situ heat treatment to obtain the desired crystalline phase. All films showed good adhesion to different substrates. After the crystallization process, the films deposited on different substrates were characterized through X-ray diffraction, UV-Vis spectroscopy and atomic force microscopy (AFM) trechniques. It was observed that an increase in the annealing temperature of the film results in an increase in the degree of crystallization and a decrease in the value of band gap energy, which was calculated from the UV-VIS spectra. The AFM analysis showed that changing the type of substrate does not influence the structural properties and microstructure of the films. By carrying out measurements of electrical resistance, it was observed that the crystalline films subjected to a ex-situ heat treatment at 500oC for 4 hours showed a good sensitivity to the ozone gas being possible to detect the presence of up to 75 ppb ozone.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-08-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.