Mémoire de Maîtrise
DOI
10.11606/D.76.1997.tde-14082009-123550
Document
Auteur
Nom complet
Fábio Becker Guedes
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1997
Directeur
Jury
Bonagamba, Tito Jose (Président)
Faria, Roberto Mendonça
Moraga, Guillermo Antonio Gonzalez
Titre en portugais
Estudo dos compostos intercalados Lix MoS2 e Lix(POE)y MoS2 utilizando-se espectroscopia de alta resolução e relaxação em sólidos por RMN
Mots-clés en portugais
Compostos intercalados
Condutores iônicos
RMN do estado sólido
Resumé en portugais
Compostos intercalados de lítio sac considerados materiais apropriados para eletrodos de baterias recarregáveis de lítio. O conhecimento das taxas de difusão, assim como os mecanismos relacionados com a mobilidade dos íons nos espaços interlaminares são portanto pertinentes para a caracterização das propriedades deste tipo de compostos. Investigações por ressonância magnética nuclear tem um papel ativo no estudo do comportamento dinâmico e estrutural destes compostos de lítio sólidos. Por essa razão este trabalho e baseado nos espectros de RMN obtidos entre 150K e 400K em um campo de 2T. As larguras de linha do 1H e do Li+ foram medidas a partir da transformada de Fourier dos FIDs resultantes da excitação da amostra por um pulse π/2. O desacoplamento de 1H foi utilizado, quando necessário, para excluir a contribuição dipolar magnética a destes núcleos a largura de linha do 7Li. Os tempos de relaxação spin-rede para os núcleos 7Li e 1H foram obtidos utilizando-se o método de inversão-recuperação. A partir destas medidas, diversos parâmetros dinâmicos e estruturais destes compostos foram encontrados como: energias de ativação, tempos de correlação e coeficientes de difusão dos íons lítio.
Titre en anglais
Study of intercaled compounds LixMoS2 and Lix(POE)yMOS2 using high resolution spectroscopy and relaxation in solids by NMR.
Mots-clés en anglais
Intercaled compounds
Ionic conductors
Solid state NMR
Resumé en anglais
Lithium intercalation compounds are considered suitable materials for electrodes in rechargeable lithium batteries. The knowledge of diffusion rates as well as of mechanistic features related with the mobility of ions in the interlamellar spaces is therefore relevant for the regulation of the properties of this kind of compounds. Nuclear magnetic resonance investigations have played an active role in the study of the dynamic and structural behavior of these solid lithium compounds. For this reason this work is based on NMR spectra recorded between 150K and 400K at 2T. The 1H and Li+ linewidths were measured from the Fourier transform of the FIDs following a π/2 excitation. IH decoupling was used, when necessary, to exclude the magnetic dipolar contribution of this nucleus to the 7Li linewidth. The 7Li and 1H spin-lattice relaxation time T1 were measured using the inversion-recovery method. Several dynamic and structural NMR parameters were obtained from these NMR measurements like activation energies, correlation times and diffusion coefficients.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-08-31
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.