• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.76.2000.tde-13122013-103359
Documento
Autor
Nombre completo
Cassio de Campos Tambelli
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Gonzalez, Jose Pedro Donoso (Presidente)
Maule, Agnieszka Joanna Pawlicka
Souza, Ernesto Chaves Pereira de
Título en portugués
Ressonância magnética nuclear (1H e 7Li) dos compósitos formados por POE: LiCl04 e aluminas
Palabras clave en portugués
Compósitos de eletrólitos poliméricos
Ressonância magnética nuclear
Resumen en portugués
Os eletrólitos poliméricos formados com base de poli(óxido de etileno) POE e um sal alcalino, vem sendo motivo de grande interesse científico devido ao seu potencial de aplicações em dispositivos eletroquímicos. A condutividade iônica nestes sistemas resulta do fato que a macromolecula atua como solvente para o sal, deixando-o parcialmente dissociado. Neste trabalho, foi utilizada a técnica de Ressonância Magnética Nuclear (RMN) para caracterizar as dinâmicas do spin nuclear do 1H e do 7Li findando investigar os mecanismos de transporte iônico dos compósitos de eletrólitos poliméricos baseados no POE8:LiC104 e partículas de &3945; e γ-alumina. Foram feitas medidas da forma da linha de ressonância e da relaxação spin-rede nas frequências de 36 MHz (1H) e 155,4 MHz (7Li) em função da temperatura no intervalo de 170-350 K. Caracterizações fisicas das partículas foram realizadas através das medidas de tamanho de partícula, porosidade e área superficial. Nos compósitos foram feitas medidas de análise témica por DSC e de condutividade elétrica ac por impedância complexa. Os resultados de RMN do 1H mostraram uma maior mobilidade das cadeias poliméricas para o compósito preparado com a dispersão de 20% de α-Al203 em massa, em relação ao eletrólito polimérico sem partículas. Nenhuma alteração foi observada nas medidas de largura de linha e relaxação spin-rede para os compósitos preparado com 5% de α ou γ-alumina. A mobilidade dos íons Li+ apresenta um aumento quando é disperso 20% de α-alumina no complexo polimérico. Em contrapartida, a adição de 20% de γ-alumina não altera os valores da taxa de relaxação (1/T1), porém um estreitamento da linha de ressonância em baixas temperaturas, em relação ao complexo polimérico, é observado. Os resultados serão discutido com base nas interações de ácido-base de Lewis
Título en inglés
Nuclear magnetic resonance (1H and 7Li) of the PEO: LiCl04 and alumina composites
Palabras clave en inglés
NMR
Nuclear magnetic resonance
Polymer electrolyte composites
Resumen en inglés
Polymeric electrolytes based on poly(ethylene oxide) (PEO) and alkaline salts has been subject of scientific and technological interest due to its potential applications as solid electrolytes in electrochemical devices. The ionic conductivity of such electrolytes results from the fact that the macromolecule acts as a solvent for the salt, leaving it partially dissociated. Nuclear magnetic resonance (NMR) techniques were used to characterize the 1H and 7Li nuclear spin dynamics in order to investigate the transport properties associated to the ionic conduction mechanisms of polymeric composites based on PEO8:LiC1O4 and particles of α and γ-alumina. NMR lineshapes and spin-lattice relaxation were measured at 36 MHz (1 H) and 155.4 MHz (7Li) as a function of temperature in the range of 170-350 K. Physical characterization of the particles was realized by measuring the particle size distribution, porosity and superficial area. Differential scanning calorimetry (DSC) and ac electric conductivity of the composites were measured. 1H NMR results show that the polymeric chains of the composite prepared with 20 wt.% of α-alumina has a greater mobility if compared with the unfilled polymeric material. No changes in linewidth and relaxation rates were observed following the addition of 5 wt.% of α or γ-alumina. The 7Li mobility increases when 20 wt.% of &3945;-alumina is added to the starting polymeric material. On the other hand, addition of 20 wt.% of γ-alumina do not alter the relaxation rates but produces a small change in linewidth. Results are discussed in accordance with the Lewis acid-base interaction
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
CassioTambelliM.PDF (67.99 Mbytes)
Fecha de Publicación
2013-12-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.