Tesis Doctoral
DOI
10.11606/T.76.2004.tde-11112013-150338
Documento
Autor
Nombre completo
Carla Eiras
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2004
Director
Tribunal
Goncalves, Debora (Presidente)
Faria, Roberto Mendonça
Gobato, Yara Galvão
Nart, Francisco Carlos
Temperini, Marcia Laudelina Arruda
Título en portugués
Eletrossíntese e propriedades ópticas e morfológicas de filmes de poli-p-fenileno e derivados
Palabras clave en portugués
Copolímeros
Eletrossíntese
Poli-p-fenileno
Resumen en portugués
Nesta tese, estudamos a eletrossíntese de polímeros conjugados eletroluminescentes no azul. Filmes de poli(p-fenileno) (PPP), co-poli(p-fenileno-pirrol) (CPPI) e co-poli(p-fenileno-3-metiltiofeno) (CFMET) foram preparados por voltametria cíclica em eletrodos de vidro condutor (ITO) em uma solução não-aquosa de acetonitrila e perclorato de tetrabutilamônio contendo os monômeros e pares de co-monômeros a diferentes concentrações. Durante a síntese dos filmes de PPP, CPPI e CP3MET, a célula eletroquímica foi posicionada dentro de uma caixa seca contendo CaCl2 como agente secante e em atmosfera de N2(g) super-seco com o objetivo de reduzir a umidade do ar no meio de síntese. A baixa umidade do ar obtida durante as medidas permitiu o controle de parâmetros de crescimento dos filmes de PPP e de seus derivados (CPPI e CP3MET). A morfologia dos filmes foi correlacionada aos seus valores de espessura e de rugosidade obtidos por microscopia de força atômica (AFM). As propriedades ópticas dos filmes foram também investigadas por espectroscopia no UV-VSNIR em função do número de ciclos da varredura obtidos durante a eletrossíntese. As respostas eletroquímicas, dos filmes de FPP, CPPI e CP3MET foram obtidas por voltametria cíclica em uma solução livre de monômero. Estes filmes tiveram ainda a confirmação de suas estruturas químicas por meio de resultados obtidos por espectroscopia no infravermelho (FTIR) e por microespectroscopia e mapeamento Raman
Título en inglés
Electrosynthesis, optical and morphological properties of poly-p-phenylene films and derivatives
Palabras clave en inglés
Copolymers
Electrosynthesis
Poly-p-phenylene
Resumen en inglés
This work describes the electrochemical synthesis of poly(p-phenylene) (PPP), p-phenylene-pyrrole copolynier (GPPIC) and p-phenylene-3methylthiophene copolymer (CP3MET). The main interest in studying these materials comes from its blue-electroluminescent properties, which make them suitable for application in electroluminescent devices. The polymerization was carried out using cyclic voltammetry in an acetonitrile non-aqueous medium containing tetrabutylammonium perchlorate and different concentration of each monomer. All the films were synthesized onto indium-tin-oxide covered glass (EO) electrodes. In order to enhance the film quality, electropolymerization was carried out within a glove box containing CaCl2, which was added as a drying agent, and under N2 atmosphere. The low amount humidity during the measurements allowed us to correlate the morphological, electrochemical and optical properties of the films of PPP and derivatives (CPPI and CP3MET). The optical properties of the films were investigated by UV-VIS-NIR spectroscopy after varying the number of cyclos reached during the preparation of the films. The electrochemical response of the films was analyzed via cyclic voltammetry using a monomer-free electrolytic solution. The morphology of the films was correlated to their values of thickness and roughness as obtained by using atomic force microscopy (AFM) and the structural characterization of PPP e their derivatives were obtained by micro-Raman spectroscopy and Raman mapping.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
CarlaEirasD.pdf (8.15 Mbytes)
Fecha de Publicación
2013-11-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.