• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.76.2001.tde-06102008-161139
Documento
Autor
Nombre completo
Claudia Maria Nicoli Candido
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2001
Director
Tribunal
Li, Maximo Siu (Presidente)
Nunes, Luiz Antonio de Oliveira
Pontuschka, Walter Maigon
Título en portugués
Propriedades ópticas de vidros oxifluoroboratos de chumbo dopados com DY3+.
Palabras clave en portugués
Espectroscopia óptica
Luminescência
Terras-raras
Vidros oxifluoroboratos de chumbo
Resumen en portugués
Este trabalho apresenta o estudo de propriedades espectroscópicas de Vidros Oxifluoroboratos de Chumbo, 40PbO-10PbF2-50B2O3 dopados com diferentes concentrações de Dy3+: 1, 3, 5 e 7 mol%. Para tanto foram empregadas as técnicas de Difração de Raios-X, Espalhamento Raman, Absorção Óptica e Fotoluminescência. Parâmetros como temperatura de transição vítrea, índice de refração e densidade também foram determinados. O comportamento do índice de refração, da densidade, e da temperatura de transição vítrea, Tg, indicaram uma possível mudança estrutural provocada pela adição de dopante, o que foi confirmado pela Espectroscopia Raman. Com as medidas de absorção óptica foram calculados os parâmetros fenomenológicos de Judd-Ofelt, Ωλ (λ = 2, 4, 6), com os quais se calculou as probabilidades de transição radiativa do íon, bem como se verificou o caráter covalente das ligações presentes na matriz. As medidas de Fotoluminescência mostraram que o aumento da concentração de dopante diminui a intensidade da emissão, e que a diminuição da temperatura provoca um aumento da intensidade das mesmas bem como promove o estreitamento das bandas de emissão. Além disto, foi possível verificar a dependência da intensidade da emissão com a energia de excitação utilizada. Para as medidas de Fotoluminescência em baixas temperaturas foi desenvolvido um sistema alternativo baseado numa sonda de fibra óptica cuja utilização mostrou-se mais simples que a tradicional montagem com criostato.
Título en inglés
Optical espectroscopy of lead oxifluoroborates glasses doped with Dy3+.
Palabras clave en inglés
Lead oxyfluoroborate glasses
Luminescence
Optical spectroscopy
Rare-earth
Resumen en inglés
This work presentes the study of the spectroscopic properties of Lead Oxifluroborate Glasses, 40PbO-10PbF2-50B2O3 doped with four different concentrations of Dy3+: 1, 3, 5 e 7 mol%. In order to achieve this, X-ray diffraction, Raman scaterring, Optical absorption, and Photoluminescence techniques were applied. Important parameters like the glass transition temperature, the index of refraction, and the density were also obtained. The behavior of these parameters suggested a possible structural change induced by adding Dy3+: which was confirmed by Raman scattering. The Judd-Ofelt phenomenological parameters, Ωλ (λ = 2, 4, 6), were calculated from the optical absorption results. From these values the ion radioactive transition probability were obtained and the covalent character of the bonds in the matrix was established. The photoluminescence measurements showed that an increase of Dy3+: concentration diminishes the emission intensity. The opposite happens decreasing the temperature, which also narrows the emission bands. Additionally, the emission intensity dependence with the excitation energy was verified. In order to study photoluminescence in the low temperatures range it was developed an alternative system based on an optical fiber probe. This device revealed to be more simple to operate than cryostat traditional system.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-10-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2023. Todos los derechos reservados.