Disertación de Maestría
DOI
10.11606/D.76.1996.tde-06022014-110700
Documento
Autor
Nombre completo
Cristina Tereza Monteiro Ribeiro
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1996
Director
Tribunal
Nunes, Luiz Antonio de Oliveira (Presidente)
Li, Maximo Siu
Vieira Junior, Nilson Dias
Título en portugués
Espectroscopia optica dos ions terras raras Er+3 e Gd+3 em vidros fluoroindatos
Palabras clave en portugués
Espectroscopia óptica
Terras raras
Vidros
Resumen en portugués
Este trabalho consiste na caracterização óptica dos íons terras raras Er+3, Yb+3 e Gd+3 quando em vidros fluoroindatos. As técnicas utilizadas foram: absorção óptica, luminescência e tempo de vida. Foram realizadas medidas de upconversion em vidros dopados com os íons Er+3 e Yb+3 nas concentrações de 2% mol de ErF3 e concentrações de 0, 2 e 8% mol de Yb+3 com excitação em 0.8 e 0.98μm observando as transições 2H11/24I15/2 4S3/24I15/2 (verde) e 4F9/24I15/2 (vermelho). Como resultado verificou-se que o Yb+3 aumenta a eficiência da emissão por upconversion no vermelho. Através de medidas espectroscópicas nos vidros fluoroindatos com Gd+3 não foi verificado tendência a cristalização destes vidros, mesmo para altas concentrações de Gd+3 Para o íon Gd+3em vidros fluoroindatos foram determinados os parâmetros de Judd-Ofelt, através dos quais determinamos as propriedades ópticas do íon e comparamos com os dados obtidos experimentalmente. Estes resultados se encontram em boa concordância
Título en inglés
Spectroscopy properties of fluoride glasses doped with Er+3 and Gd+3
Palabras clave en inglés
Glass
Rare earth
Spectroscopy
Resumen en inglés
This work consists of the optical characterization of rare earth Er+3, Yb+3 and Gd+3 fluoroindate glasses by means of luminescence, optical absorption and lifetime techniques. Upconversion process were studied in Er+3, Yb+3 doped glasses (with the same ErF3 concentration and different Yb+3 concentrations) excited at 0.8 and 0.98μm. Transitions 2H11/24I15/2 4S3/24I15/2 (green) e 4F9/24I15/2 (red) were detected. As a result, we conclude that the Yb+3 incorporation increases the emission efficiency of the red upconversion process. Spectroscopic measurements performed on Gd+3 fluoroindate glasses didn't point out crystallization tendency of the glasses, even for high Gd+3 concentrations. The Judd-Ofelt parameters of Gd+3 fluoroindate glasses were obtained, so that the optical properties of Gd+3 were determined. The results are in good agreement with the experiment
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-02-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.