Disertación de Maestría
DOI
10.11606/D.76.2001.tde-05112008-121104
Documento
Autor
Nombre completo
Silmar Antonio Travain
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2001
Director
Tribunal
Giacometti, José Alberto (Presidente)
Job, Aldo Eloizo
Mastelaro, Valmor Roberto
Título en portugués
Preparação e caracterização de filmes de polianilina pelo método de disposição "in situ".
Palabras clave en portugués
Cinética de adsorção
Deposição "in-situ"
Morfologia de superfície
Polianilina
Resumen en portugués
Neste trabalho otimizou-se uma metodologia para a deposição de filmes de polianilina, PAni, na qual o substrato de vidro é inserido na solução em que se realiza a polimerização. Este método de deposição "in situ", feito a temperatura de O °C, permite obter filmes com boa uniformidade e com controle de espessura. A espessura dos filmes, da ordem de centenas de nanômetros, pode ser controlada através da concentração da solução do meio reacional. A morfologia da superfície do filme foi estudada usando a técnica de microscopia de força atômica. Os resultados mostraram que a rugosidade aumenta com a diminuição da concentração e com o tempo de deposição da camada de PAni. Para demonstrar a aplicação dos filmes de PAni foi construído um dispositivo eletroluminescente tendo o poli(-fenileno vinileno)-dodecilbenzeno sulfonato de sódio, PPV-DBS, como polímero ativo e usando uma camada de PAni como eletrodo injetor de buracos e janela transparente para a saída da luz. Mostrou-se que o dispositivo opera com uma tensão aproximadamente 3 vezes menor em comparação com um dispositivo sem a camada de PAni.
Título en inglés
Preparation and characterization of polyaniline films by the "in-situ" deposition method.
Palabras clave en inglés
"In-situ" deposition
Adsorption kinetics
Polyaniline
Surface morphology
Resumen en inglés
A method for deposition of polyaniline, PAni, onto glass substrates was studied. Substrates were inserted in the solution in which the polymerization reaction occurs. This method performed "in situ", at the temperature of 0 °C, gives very uniform films and allows the control of the thickness. Thickness, of the order of hundred nm, can be controlled varying the concentration of the solution in which the polymerization occurs. The morphology of the PAni layer was studied using a force atomic microscope, AFM. The roughness increased on the time of deposition of the layer and with the decrease of the concentration of the solution. In order to demonstrate the use of the PAni layer an electro luminescent device was built using as active polymer poly(-fenylene vinylene) -dodecilbenzene sulphonate of sodium, PPV-DVS, and the PAni layer as injector of holes and was transparent window for the emitted light. The device showed that it could be operated with a voltage that is three times smaller than a corresponding device without the PAni layer.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-10
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.