Tese de Doutorado
DOI
10.11606/T.75.2017.tde-30032017-091831
Documento
Autor
Nome completo
Ricardo Bertholo Valim
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2016
Orientador
Banca examinadora
Lanza, Marcos Roberto de Vasconcelos (Presidente)
Mazo, Luiz Henrique
Mascaro, Lucia Helena
Motheo, Artur de Jesus
Olivi, Paulo
Título em português
Desenvolvimento e aplicação de eletrodos de difusão gasosa (EDG) modificados com óxidos bimetálicos de Ru e Nb em carbono amorfo para a eletrogeração de H2O2
Palavras-chave em português
carbono Printex 6L
eletrodos de difusão gasosa
eletrogeração
Materiais bimetálicos
peróxido de hidrogênio
Resumo em português

Neste trabalho foram estudadas a atividade e seletividade de materiais bimetálicos de rutênio e nióbio, adicionados em matriz de carbono do tipo Printex 6L, para a eletrogeração de peróxido de hidrogênio a partir da reação de redução de oxigênio. Os materiais foram caracterizados por aplicação de técnicas eletroquímicas em microcamada porosa e em eletrodos de difusão gasosa, em meio ácido. Foram realizados estudos de caracterização física e morfológica dos materiais para a compreensão dos possíveis óxidos formados em substrato de carbono, por análises de difração de Raios-X, por fluorescência de Raios-X, por microscopia eletrônica de varredura acoplada a um sistema de espectroscopia de Raios-X por dispersão de energia. Por caracterização eletroquímica em microcamada porosa, o material com 5,0% de Ru05%Nb95%Oz em carbono foi escolhido como o material com maior seletividade para a eletrogeração de peróxido de hidrogênio, com eficiência de corrente calculada de 84,6%, em potencial aplicado de -0,515 V (vs. Ag/AgCl), sendo posteriormente estudado em eletrodo de difusão gasosa, por cronopotenciometria, com concentração de peróxido de hidrogênio eletrogerado de 210,74 mg L-1, em 90 minutos de experimento, com uma densidade de corrente de -100 mA cm-2, cerca de 24,5% maior quando comparada a eletrogeração de H2O2 detectada para a matriz de carbono térmico, sem adição de elementos metálicos, nas mesmas condições experimentais. Os resultados de constante cinética obtidos na mesma densidade de corrente aplicada de -100 mA cm-2, foram: de 2,44 mg L-1 min-1 para o material com 5,0% de Ru05%Nb95%Oz, e de 1,78 mg L-1 min-1 para o eletrodo de difusão gasosa sem modificador.

Título em inglês
Development and application of gas diffusion electrodes (EDG) modified with bimetallic oxides of Ru and Nb in amorphous carbon for H2O2 electrogeneration.
Palavras-chave em inglês
Bimetallic materials
diffusion gas electrode
electrogeneration
hydrogen peroxide
Printex L6 carbon
Resumo em inglês

In this work, the activity and selectivity of bimetallic materials composed by ruthenium and niobium, added on carbon matrix Printex 6L, for electrogeneration of hydrogen peroxide from oxygen reduction reaction. The materials were characterized by the application of electrochemical techniques in porous microlayer and gas diffusion electrodes, in acid medium. The physical and morphological characterization were made of the materials for understanding the possible metallic oxides formation in carbon substrate by analysis of X-rays diffraction , X-rays fluorescence , by scanning electron microscopy coupled by an energy-dispersive X-ray spectroscopy. For electrochemical characterization using porous microlayer, the material with 5.0% of Ru05%Nb95%Oz in carbon was chosen as the material with greater selectivity for the hydrogen peroxide electrogeneration, with calculated current efficiency of 84.6% in applied potential of -0.515 V (vs. Ag/AgCl), studied using a gas diffusion electrode, by chronopotentiometry, with obtained hydrogen peroxide concentration of 210.74 mg L-1, at 90 minutes of experiment, with a the current density of -100 mA cm-2, about 24.5% higher when compared with the hydrogen peroxide electrogeneration detected for a carbon matrix, without addition of metal elements, under the same experimental conditions. The results obtained for calculated kinetic constant, using the same applied current density of -100 mA cm-2: 2.44 mg L-1 min-1 for using the material with 5.0% Ru05%Nb95%Oz, and 1.78 mg L-1 min-1 for using the carbon matrix without modification.

 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2017-03-30
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.