Thèse de Doctorat
DOI
10.11606/T.75.2015.tde-26102015-114419
Document
Auteur
Nom complet
Kelen Menezes Flores Rossi de Aguiar
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Rodrigues Filho, Ubirajara Pereira (Président)
Eckert, Hellmut
Goncalves, Debora
Plepis, Ana Maria de Guzzi
Rischka, Klaus
Titre en portugais
Síntese de hidroxiuretana-poli(dimetilsiloxano) com diferentes terminações de cadeia via fixação de CO2: síntese, caracterizações e potenciais aplicações
Mots-clés en portugais
filmes híbridos
fixação de CO2
hidroxiuretanas
polidimetilsiloxano
Resumé en portugais
Neste trabalho uretanas livres de isocianatos produzidas a partir de um precursor bis(ciclocarbonato) oligomérico contendo segmentos de poli(dimetil siloxano) (CCPDMS) foram sintetizadas. Para tal, utilizou-se diferentes aminas primárias como a 3-aminometil-3,5,5 trimetilciclohexilamina (IPDA) e as monoaminas 3-aminopropil(trietóxisilano) (APTES), feniletilamina (PEA), catecol amina (dopamina) e um decapeptídeo derivado da proteína de adesão de mariscos (mefp-1).O precursor oligomérico CCPDMS foi produzido por fixação de dióxido de carbono em anéis epóxi catalisado por um sal quarternário de amônio, o brometo de tetraetilamônio (BTA). O precursor CCPDMS foi então reagido com as aminas por meio de polimerização por abertura de anel formando hidroxiuretanas derivadas de PDMS (PDMSUr) com diferentes terminações de cadeia. Tendo como terminador de cadeia o APTES, foi possível produzir um material híbrido com domínios inorgânicos de sílica organicamente modificada (ormosil) interligadas com a parte orgânica de PDMS por meio de ligações uretana. Nesta matriz híbrida foram adicionadas diferentes porcentagens mássicas de ácido fosfotúngstico (PWA), variando entre 1% a 55%. Os materiais foram caracterizados quanto à sua estrutura química por técnicas espectroscópicas (Ressonância Magnética Nuclear, Infravermelho, Espectroscopia de Fotoelétrons, MALDI-ToF), propriedade anti-corrosão (espectroscopia de impedância eletroquímica, polarização potenciodinâmica), propriedades superficiais (energia livre superficial, nanoindentação), análise morfológica (Microscopia Eletrônica de Varredura), estabilidade térmica (Análise Termogravimétrica), testes de adesão (pull-off-test e cisalhamento), testes microbiológicos (adesão de bactérias, tecidos e citotoxicidade), além de ensaios de fotocromismo. O polioxometalato PWA conferiu propriedades fotocrômicas aos filmes híbridos de PDMSUr com máxima absorbância de 1,6 u.a após irradiação por luz ultra-violeta (UV). PDMSUr híbridas com ou sem PWA foram testadas como adesivos para vidro, alumínio, aço (SS316L) e liga de titânio (Ti6Al4V) apresentando valores de força de adesão entre 2-7 MPa. Filmes de PDMSUr preparados em diferentes substratos apresentaram comportamento bacteriostático frente à adesão de Escherichia coli (E.coli) e Lactobacillus casei (L.casei). A PDMSUr biomimética terminada por grupos catecóis foi capaz de formar camadas em superfícies metálicas apresentando boa estabilidade frente à remoção da camada depositada por lavagem com etanol.
Titre en anglais
Synthesis of hydroxyurethanes-poly(dimethylsiloxane) with different chain terminations via carbon dioxide fixation: Characterizations and potential applications.
Mots-clés en anglais
CO2 fixation
hybrid films
urethanes PDMS derived
Resumé en anglais
Free isocyanate urethanes produced from an oligomeric precursor bis(cyclic carbonate) bearing poly(dimethylsiloxane) (CCPDMS) were synthesized in this work. Different primary amines such as 3-Aminomethyl-3,5,5-trimethylcyclohexylamine (IPDA) and monoamines 3-aminopropyltriethoxysilane (APTES), phenylethylamine (PEA), catechol amine (dopamine) and a decapeptide derived from marine mussel foot protein (mefp-1). The precursor cyclic carbonate CCPDMS was obtained from carbon dioxide fixation into epoxy rings catalized by a quaternary ammonium salt, tetraethylamonium bromide (TEAB). The precursor CCPDMS was reacted with the different amines by ring opening polymerization affording the formation of hydroxyurethanes PDMS derived (PDMSUr) with different chain terminations. Using APTES as chain terminator was feasible to obtain a hybrid material containing inorganic domains of organically modified silica (ormosil) interconnected to the organic part PDMS through urethane bond. In this hybrid matrix different mass percentages, varying from 1%wt to 55 wt%, of phosphotungstic acid (PWA) were added. The materials were characterized regarding their chemical structure by spectroscopic techniques (Nuclear Magnetic Resonance, Infrared, and X-ray photoelectron spectroscopy), mass spectrometry (MALDI-ToF and GPC), anti corrosive property (Electrochemical Impedance Spectroscopy and potentiodynamic polarization), surface properties (free surface energy, nanoindentation), morphology (Scanning Electron Microscopy), thermal stability (Thermogravimetric analysis), adhesion strenght measurements (pull-off-test and lap-shear), microbiologic assays (bacteria adhesion, tissue adhesion and citotoxicity test) besides photochromic assays. The polyoxometalate PWA provided photochromic property to the PDMSUr hybrid films presenting a maximum absorbance of 1.6 a.u after ultraviolet (UV) irradiation. Hybrids PDMSUr with or without PWA were tested as adhesive for glass, aluminium, steel (SS316L) and titanium alloy (Ti6Al4V) showing adhesion strength values ranging from 2-7 MPa. PDMSUr films prepared on different substrates showed bacteriostatic behavior against Escherichia coli (E.coli) and Lactobacillus casei (L.casei). The biomimetic PDMSUr catechol endcapped was able to form a layer on metallic surfaces showing good stability after rinsing with ethanol.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-10-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.