Master's Dissertation
DOI
https://doi.org/10.11606/D.75.2024.tde-21032024-111407
Document
Author
Full name
Giovanna Ferreira Bigotto Gonçalves
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2024
Supervisor
Committee
Manzani, Danilo (President)
Rodrigues, Lucas Carvalho Veloso
Teodoro, Marcio Daldin
Title in Portuguese
Compósitos luminescentes de poliuretanas a base de óleo de mamona incorporados com quantum-dots para aplicações em fotônica
Keywords in Portuguese
luminescência
luz branca
optoeletrônicos
poliuretanas
quantum-dots
Abstract in Portuguese
Este trabalho apresenta o estudo e desenvolvimento de películas compósitas de poliuretanas à base de óleo de mamona contendo quantum-dots (QD), com o objetivo final de produzir um compósito emissor de luz branca, por meio da soma de cores do tipo RGB. Os QD se destacam por apresentarem eficientes propriedades ópticas e luminescentes e para torná-las aplicáveis devem estar contidos em matrizes que oferecem estabilidade sem alterar suas propriedades químicas e físicas, possibilitando sua aplicação em dispositivos optoeletrônicos. As soluções de QD de tipo CdSe, foram obtidas por meio da síntese coloidal em injeção à quente (hot-injection) sendo seu agente de superfície ácido oleico. As propriedades luminescentes dos QD foram analisadas por espectroscopias de absorção, emissão e excitação, e sua distribuição de tamanhos por microscopia eletrônica de transmissão (MET). Os resultados indicaram máximos de emissão em 575 nm, 620 nm e 675nm. As amostras foram sintetizadas mantendo a composição da matriz polimérica e variando a concentração de QD e suas dimensões. Após a incorporação no polímero, as amostras foram analisadas por técnicas de caracterização, como a espetroscopias de absorção e emissão, espectroscopia no infravermelho por transformada de Fourier (micro-FTIR), MET e microscopia de fluorescência. Após a análise de suas propriedades luminescentes, os resultados indicaram luminescência, com emissões por parte do próprio polímero em 464 nm e emissões relacionadas as soluções coloidais de QD em 600 nm, 625 nm e 675 nm, provocando o efeito de red-shift em QD de menores dimensões. O espectro de micro-FTIR não indica interferência pela adição das soluções coloidais no processo de polimerização da matriz. Nas imagens de MET é possível constatar a presença de aglomerados de QD, com diâmetros maiores que 100nm, proveniente de rearranjos dentro da cadeia polimérica. No entanto, os resultados por meio da microscopia de fluorescência não indicam a desativação de QD após a formação de aglomerados e que estes ainda apresentam uma luminescência significativa.
Title in English
Luminescent composites of castor oil-based polyurethanes incorporated with quantum dots for photonic applications
Keywords in English
luminescence
optoelectronics
polyurethanes
quantum dots
white light
Abstract in English
This work encompasses a comprehensive investigation and development of composite films based on castor oil-derived polyurethane, incorporating quantum dots (QDs) with the ultimate goal of creating a composite material that emits white light through the additive blending of RGB colors. Quantum dots are particularly notable for their remarkable optical and luminescent properties. To harness these properties effectively, it is imperative to encapsulate them within matrices that ensure stability without compromising their intrinsic chemical and physical characteristics. This is a crucial prerequisite for their utilization in optoelectronic devices. The CdSe-type QD solutions were synthesized through a hot-injection colloidal method with oleic acid serving as the surface agent. The luminescent characteristics of these QDs were meticulously examined through absorption, emission, and excitation spectroscopy, and their size distribution was assessed using transmission electron microscopy (TEM). The results revealed emission peaks at 575 nm, 620 nm, and 675 nm. To create the composite samples, the polymer matrix composition remained consistent, while the QD concentration and dimensions were varied. Subsequently, following the incorporation of QDs into the polymer matrix, the samples underwent thorough characterization using techniques such as absorption and emission spectroscopy, Fourier-transform infrared spectroscopy (micro-FTIR), MET, and fluorescence microscopy. The analysis of their luminescent properties indicated emissions originating both from the polymer itself, with a peak at 464 nm, and from the colloidal QD solutions, exhibiting peaks at 600 nm, 625 nm, and 675 nm. This resulted in a red-shift effect for smaller QDs. Notably, the micro-FTIR spectrum revealed no interference due to the addition of colloidal solutions during the polymerization process. Transmission electron microscopy (MET) images depicted the presence of agglomerates from QD, with diameters more than 100nm, likely arising from rearrangements within the polymer chains. However, the results from fluorescence microscopy not suggested deactivation after the formation of these agglomerates and shows a significant luminescence.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2024-04-02
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.