Doctoral Thesis
DOI
10.11606/T.75.2015.tde-17042015-093852
Document
Author
Full name
Dyovani Coelho
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2015
Supervisor
Committee
Machado, Sergio Antonio Spinola (President)
Albuquerque, Hamilton Brandão Varela de
Dall'Antonia, Luiz Henrique
Garcia, Jarem Raul
Pedrosa, Valber de Albuquerque
Title in Portuguese
Utilização da eletrodeposição em regime de subtensão na dopagem de filmes semicondutores eletrodepositados de selênio
Keywords in Portuguese
Deposição em regime de subtensão
Selênio
Semicondutores
Abstract in Portuguese
A deposição em regime de subtensão (DRS) tem sido amplamente utilizada para a formação de filmes semicondutores, mas muito pouco utilizada para estudar a dopagem de filmes eletrodepositados. Logo, neste trabalho é discutido o uso da DRS como técnica de dopagem de filmes de selênio. Para isso, estudou-se as condições de deposição de um filme de selênio trigonal sobre substrato de ouro (f-Se) e sua posterior modificação com a DRS de Bi (f-Se_Bi), Pb (f-Se_Pb) e Cu (f-Se_Cu). Estudos empregando voltametria cíclica, cronoamperometria, microscopia óptica, microscopia de varredura eletrônica e difração de raio-X evidenciaram a produção de um filme altamente cristalino, homogêneo e aderente formado por estruturas hexagonais em forma de microbastões com diâmetros entre 300 e 600 nm. Contudo, o filme com as características citadas é formado somente com a deposição a 80 ºC em HNO3 0,1 mol L-1 contendo SeO2 0,02 mol L-1, com polarização do substrato em -0,45 V (vs SCE), sob iluminação com lâmpada de halogênio 100 W, irradiância de 200 mW cm-2, agitação magnética e tempos de deposição ≥ 600 segundos. Essas estruturas são mantidas mesmo após a DRS dos metais, a qual foi caracterizada empregando a microbalança eletroquímica de cristal de quartzo (MECQ). A partir do perfil massométrico constatou-se a ocorrência de difusão dos metais para o interior da fase de selênio, visto que não se observou a saturação da superfície do filme. Além disso, os metais apresentam cinética de difusão diferentes, onde o metal com maior difusão é o cobre, sendo o único a apresentar dopagem efetiva da matriz de selênio. A caracterização óptica dos filmes determinou um band gap de aproximadamente 1,87 ±0,03 eV para f-Se, f-Se_Pb e f-Se_Bi, entretanto, o f-Se_Cu apresentou band gap de 3,19 eV. Ainda assim, ao avaliar a atividade fotoeletroquímica dos semicondutores constatou-se a obtenção de fotocorrentes distintas entre eles. O f-Se_Bi produz fotocorrente 3 vezes maior que o f-Se_Pb e 35 vezes mais elevada que os demais, embora o selênio puro e os filmes dopados com DRS de Bi e Pb apresentem densidade de portadores de carga similares, aproximadamente 6,0 x1015 cm-3, enquanto o f-Se_Cu exibe um aumento de 4 ordens de grandeza para o mesmo parâmetro. Logo, a elevada fotocorrente do filme f-Se_Bi está relacionada com a minimização da recombinação de cargas na interface semicondutor-eletrólito, enquanto a baixa fotocorrente exibida pelo f-Se_Cu se deve à elevada energia de band gap do filme. De qualquer forma, a dopagem de filmes semicondutores com a DRS mostrou ser uma maneira simples e barata de dopagem de filmes relativamente espessos.
Title in English
Use of underpotential deposition in the doping of electrodeposited selenium semiconductive films
Keywords in English
Selenium
Semiconductor
Underpotential deposition
Abstract in English
The underpotential deposition (UPD) have been widely used to production of semiconductor films, but not applied to search the doping of electrodeposited films. Therefore, here is discussed the use of UPD as a technique to doping selenium films. Then, it was studied the conditions to attain deposits of trigonal selenium on gold substrate (f-Se) and after its modification with Bi UPD (f-Se_Bi), Pb UPD (f-Se_Pb) and Cu UPD (f -Se_Cu). Studies using cyclic voltammetry, chronoamperometry, optical microscopy, scanning electron microscopy (SEM) and X-ray diffraction (XRD) showed the production of a highly crystalline, homogeneous and adherent selenium film formed by hexagonal structures with microrod shape and diameters between 300 and 600 nm. However, the trigonal selenium with those features is synthezised only on the deposition into HNO3 0.1 M containing SeO2 0.02 M at 80 °C, -0.45 V (vs. SCE), under illumination with halogen lamp 100 W, irradiance of 200 mW cm-2, magnetic stirring and deposition time ≥ 600 seconds. These structures are maintained even after the UPD of the metals, which was characterized using electrochemical quartz crystal microbalance (EQCM). From massogram profile was possible to observe the occurrence of diffusion of the metals into the selenium phase, since was not verified the surface saturation of the film. Furthermore, the metals exhibited different diffusion kinetics, where the metal with higher diffusion was copper, which was the only one to show effective doping of selenium film. The optical characterization of the films determined a band gap average of 1.87 ±0,03 eV for f-Se, f-Se_Pb and f-Se_Bi, although, the f-Se_Cu presented band gap of 3.19 eV. Moreover, when it is studied the photoelectrochemical activity of the semiconductors films was noted different photocurrents between them. The f-Se_Bi produces photocurrent 3 times greater than the f-Se_Pb and 35 times higher than the other, but the pure selenium and those doped with Bi and Pb UPD present similar charge-carriers density, approximately 6.0 x1015 cm-3, while the f-Se_Cu shows an increase of 4 orders of magnitude for the same parameter. Therefore, the high photocurrent to f-Se_Bi is associated with the minimization of charge recombination at semiconductor-electrolyte interface, while the low photocurrent exhibited by f-Se_Cu is due to the higher energy band gap of the film. Anyway, the doping of the semiconductor film with the UPD proved to be a simple and inexpensive way to doping relatively thick films.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2015-04-22
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.