Tesis Doctoral
DOI
10.11606/T.75.2016.tde-06072016-143913
Documento
Autor
Nombre completo
Marco Antonio Horn Júnior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Cavalheiro, Eder Tadeu Gomes (Presidente)
Chinelatto, Marcelo Aparecido
Goi, Beatriz Eleuterio
Legendre, Alexandre de Oliveira
Tiera, Vera Aparecida de Oliveira
Título en portugués
Estudo das propriedades térmicas e mecânicas de resinas dentárias compostas preparadas com sílica e quitosana
Palabras clave en portugués
análise dinâmico mecânica
fotopolimerização
quitosana
termogravimetria
Resumen en portugués
Neste trabalho foi estudada a influência da adição de quitosana e sílica a monômeros dimetacrílicos, BisEMA e TEGDMA, por meio das técnicas de fotocalorimetria, termogravimetria e análise dinâmico mecânica. Os resultados dos experimentos de fotocalorimetria demonstraram que a quitosana pode aumentar a velocidade de polimerização e o máximo de conversão para alguns sistemas em determinadas concentrações da mesma, já a sílica tem pouco efeito nas reações de fotopolimerização das amostras. Para os experimentos de termogravimetria, a quitosana tem pouca influência na degradação das amostras não alterando significativamente as curvas TGA/DTG, por outro lado a sílica acelerou a degradação térmica das amostras. A avaliação das propriedades mecânicas demonstrou que a quitosana diminui a temperatura de transição vítrea e a resposta elástica dos sistemas não afetando os valores dos módulos de armazenamento e módulos de perda. A sílica apresentou a tendência de aumento de temperatura de transição vítrea e não alteração da resposta elástica das amostras.
Título en inglés
Evaluation of thermal and mechanical properties of resin composites prepared with silica and chitosan
Palabras clave en inglés
chitosan
dynamic mechanical analysis
photopolymerization
thermogravimetry
Resumen en inglés
In this work we studied the influence of the addition of chitosan and silica in dimethacrylic monomers, BisEMA and TEGDMA, by photocalorimetry, thermogravimetric analysis and dynamic mechanical analysis. The results of photocalorimetry experiments demonstrated that chitosan can increase the polymerization rate and the degree of conversion for some concentrations. Silica has little effect on photopolymerization reactions of samples. For thermogravimetric experiments, chitosan has little influence on the degradation of samples and does a slightly change the TGA / DTG curves, on the other hand silica accelerated thermal degradation of the samples. The evaluation of mechanical properties showed that chitosan reduces the glass transition temperature and elastic response of the samples but does not affect the values of the storage modulus and loss modulus. Silica showed an effect of increasing glass transition temperature and almost no change in the elastic response of the samples.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-07-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.