Disertación de Maestría
DOI
10.11606/D.75.2013.tde-30072013-093033
Documento
Autor
Nombre completo
David Esteban Quintero Jimenez
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Cavalheiro, Carla Cristina Schmitt (Presidente)
Gonzalez, Jose Pedro Donoso
Maule, Agnieszka Joanna Pawlicka
Título en portugués
Síntese e estudo de membranas condutoras iônicas a base de DNA-CTMA e DNA-DODA para aplicação em células solares
Palabras clave en portugués
células solares
condutividade
DNA
surfactantes
Resumen en portugués
Este trabalho apresenta os resultados da preparação e caracterização de eletrólitos poliméricos a partir de DNA-CTMA e DNA-DODA com adição de 7, 9, 10 e 11% (m/m) de LiClO4 e/ou LiI/I2. O objetivo é usar estes eletrólitos poliméricos em pequenas células solares sensibilizadas com corante (DSSC). O DNA com a massa molecular de 5,41x108 ± 1179,6 g/mol foi usado para a síntese de complexos de DNA-CTMA e DNA-DODA através da reação de substituição de DNA com os agentes surfactantes: CTMA e DODA. As amostras na forma de filmes foram caracterizadas por espectroscopia de impedância, difração de raios-X, UV-Vis, FT-IR e análises térmicas (DSC e TGA). Os espectros de FT-IR confirmaram a obtenção dos complexos de DNA-CTMA e DNA-DODA. A espectroscopia no UV/Vis revelou a presença de absorção em 260 nm atribuída às transições eletrônicas π- π* das bases nitrogenadas do DNA. As análises térmicas dos complexos de DNA-CTMA e DNA-DODA mostraram a estabilidade térmica de 226°C e 232°C e a transição vítrea de -67°C e -40,0°C, respectivamente. A difração de raios-X das amostras permitiu a determinação da porcentagem de cristalinidade sendo entre 43,74 e 63,20% para DNA-CTMA e entre 49,4 e 76,25% para DNA-DODA. Os filmes foram submetidos às medidas de condutividade iônica revelando os melhores resultados de 8,21x10-4 S/cm a 25°C para as amostras de DNA-CTMA com 10% (m/m) de LiClO4 e 2,87x10-4 S/cm para o DNA-DODA com 10% (m/m) de LiClO4. Os eletrólitos de DNA-CTMA com 9 e 10 % (m/m) de LiI/I2 e DNA-DODA com 9 e 10% (m/m) de LiI/I2 foram aplicados em pequenas células solares mostrando a eficiência de 0,14, 0,31, 0,177 e 0,66% respectivamente, valores considerados promissores para futuros estudos.
Título en inglés
Synthesis and study of ionic conductive membranes based on DNA-CTMA and DNA-DODA for application in solar cells
Palabras clave en inglés
DNA
ionic conductivity
solar cell
surfactants
Resumen en inglés
The present work describes the preparation and characterization of polymeric electrolytes of DNA-CTMA and DNA-DODA with addition of 7, 9, 10 and 11% (m/m) LiClO4 and/or LiI/I2. The objective is use of these polymer electrolytes in dye sensitized solar cells (DSSC). The DNA with molecular weight of 5,41x108 ± 1179,6 g/mol was used to synthesize DNA-CTMA and DNA-DODA complexes by substitution reaction. The obtained samples in the film form were then characterized by impedance spectroscopy, X-ray diffraction, UV-Vis, FT-IR and thermal analyses (DSC and TGA). The FT-IR spectra confirmed both, DNA-CTMA and DNA-DODA complexes obtaining. The UV-Vis spectroscopy of the samples evidenced an absorption band at 260 nm attributed to electronic transitions π-π * of DNA nitrogenous bases. The TGA and DSC analyses shoved a thermal stability of the DNA-CTMA and DNA-DODA samples of 226°C and 232°C and, glass transition of -67°C and -40°C, respectively. The X-ray diffraction allowed determining the crystallinity of 43.74 to 63.20% for the samples of DNA-CTMA and 49.4 to 76.25% for the DNA-DODA. The films were subjected to ionic conductivity measurements showing the best results of 8.21x10-4 S/cm at 25°C for the DNA-CTMA with 10% (w/w) of LiClO4 and of 2.87x10-4 S/cm for DNA-DODA with 10% (w/w) of LiClO4. Finally the electrolytes of DNA-CTMA with 9 and 10% (m/m) of LiI/I2 and of DNA-DODA 9 and 10% (m/m) of LiI/I2 were applied in small solar cells exhibiting the efficiency of 0,14, 0,31, 0,177 and 0,66%, respectively. The obtained results are promising for future investigations.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-11-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.