Mémoire de Maîtrise
DOI
10.11606/D.75.2015.tde-15092015-135733
Document
Auteur
Nom complet
Wilner Valenzuela Barrientos
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Gonzalez, Ernesto Rafael (Président)
Batista, Elisete Aparecida
Huguenin, Fritz Cavalcante
Titre en portugais
Estudo dos parâmetros operacionais de uma célula a combustível de glicerol direto utilizando uma membrana de polibencimidazol impregnada com ácido fosfórico (PBI/H3PO4) ou 1-hexil-3-metilimidazol trifluorometanosulfo
Mots-clés en portugais
1-hexil-3-metilimidazol trifluorometanosulfonato (HMI-Tf)
ácido fosfórico (H3PO4)
Células a combustível
glicerol
membrana de polibencimidazol (PBI)
Resumé en portugais

Com o aumento da população mundial, o desenvolvimento de novas fontes e conversores de energia tornou-se uma necessidade. As células a combustível mostram-se como uma alternativa viável devido principalmente a duas razões, sua alta eficiência e a utilização de combustíveis renováveis. No presente trabalho se estuda a influência da temperatura de operação e o conteúdo de álcali no combustível sobre a densidade de potencia para uma célula a combustível de glicerol direto. Como combustível foi utilizado uma solução de glicerol:KOH (1M:xM, x=0, 1, 3, 5), como membranas foram utilizados filmes de polibencimidazol impregnado com ácido fosfórico (PBI/H3PO4, relação molar 1:11) ou 1-hexil-3-metilimidazol trifluorometanosulfonato (PBI/HMI-Tf relação molar 1:1.5), e finalmente, nano partículas de Pt suportadas em carbono (60% w/w) como catalizador no ânodo e no cátodo. Em geral, o incremento da temperatura e conteúdo de álcali no combustível mostra um efeito favorável na densidade de potencia do sistema. Numa célula a combustível unitária de glicerol direto utilizando membranas de PBI/ H3PO4 e PBI/HMI-Tf foram obtidas densidades de potencia de 0.54mW.cm-2 a 175°C e 0.599mW.cm-2 a 130°C, respectivamente, para uma solução de glicerol de (1M); enquanto que, para uma solução com um conteúdo maior de álcali, glicerol:KOH (1M:5M), foram obtidas densidades de potencia maiores, 44.1mW.cm-2 a 175°C e 29mW.cm-2 a 130°C, respectivamente. O efeito combinado do incremento da temperatura e concentração de álcali no combustível mostra um efeito maior em relação ao efeito só da temperatura.

Titre en anglais
Study of the operating parameters of a direct glycerol fuel cell using a polibenzimidazole membrane impregnated with phosphoric acid (PBI/H3PO4) or 1-hexyl-3-methylimidaolium trifluoromethanesulfonate (PBI/HMI-Tf)
Mots-clés en anglais
1-hexyl-3-methylimidaolium trifluoromethanesulfonate (HMI-Tf).
Fuel cell
glycerol
Phosphoric acid (H3PO4)
polibenzimidazole membrane (PBI)
Resumé en anglais

With the increasing world population, the development of new energy sources or energy converters has become a necessity. Fuel cells show up as a viable alternative due mainly to two reasons, their high efficiency and the use of renewable fuels. In the present work we study the influence of operating temperature and alkali content in the fuel on the power density for a direct glycerol fuel cell. A glycerol:KOH (1M: xM, x = 0, 1, 3, 5) solution was used as fuels, as membranes were used polibencimidazol films impregnated with phosphoric acid (PBI/H3PO4, molar ratio of 1:11) or 1-hexyl-3-methylimidazolium trifluoromethanesulfonate (PBI/HMI-Tf), and finally, Pt nanoparticles supported on carbon (60% w / w) as catalyst in the anode and cathode. In general, increasing the temperature and alkali content in the fuel shows a favorable effect in the system power density. In a direct glycerol fuel cell using PBI/H3PO4 and PBI /HMI-Tf membranes were obtained power density of 0.54mW.cm-2 at 175°C and 0.599mW.cm-2 at 130°C, respectively, for a 1M glycerol solution; while for a glycerol solution with a higher content of alkali, glycerol:KOH (1M: 5M), were obtained higher power densities, 44.1mW.cm-2 at 175 ° C and 29mW.cm-2 at 130 ° C, respectively. The combined effect of increased temperature and alkali concentration in the fuel shows a greater effect compared to the effect of temperature only.

 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-09-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.