Tesis Doctoral
DOI
10.11606/T.75.2017.tde-08032017-163957
Documento
Autor
Nombre completo
Débora Morais Bezerra
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Assaf, Elisabete Moreira (Presidente)
Calegaro, Marcelo Luiz
Gonzalez, Ernesto Rafael
Asencios, Yvan Jesús Olortiga
Gallo, Jean Marcel Ribeiro
Título en portugués
Avaliação do desempenho de catalisadores obtidos de hidrotalcitas na reforma seca do metano
Palabras clave en portugués
Biogás
Deposição de coque
Hidrotalcita
Óxidos mistos
Reforma seca do metano
Singás
Resumen en portugués

Catalisadores ativos e estáveis, preparados a partir dos hidróxidos duplos lamelares (HDLs) contendo os cátions Ni2+, Zn2+, Al3+ e Zr4+(NiZn-Al, NiZn-AlZr e NiZn-Zr), foram avaliados na reação de reforma seca do metano. Os precursores foram caracterizados por difração de raios X, confirmando a formação das fases para as amostras de NiZn-Al e NiZn-AlZr. As espectroscopias no infravermelho/Raman elucidaram a ocorrência dos ânions (CO32-) e das moléculas de água na intercamada. A Fisissorção de nitrogênio ( método de BET) determinou a presença de poros e a área superficial específica. As formas das isotermas foram do tipo IV, de acordo com a IUPAC, e representa uma estrutura mesoporosa. A análise termogravimétrica foi utilizada para determinar a temperatura de calcinação dos precursores para obtenção dos catalisadores e as temperaturas utilizadas foram 550 °C, 650 °C e 750 °C. Os resultados de difração de raios X dos catalisadores apresentaram uma mistura de óxidos binários (NiO, ZnO, ZrO2 e Al2O3) e óxidos ternários (NiAl2O4 e ZnAl2O4). As fases de espinélios foram observadas nos catalisadores obtidos a 650°C (Ni/ZnAl-6 e Ni/ZnAlZr-6) e 750°C (Ni/ZnAl-7 e Ni/ZnAlZr-7). A redução a temperatura programada de hidrogênio (TPR-H2) forneceu informações sobre a redução do catalisador. Os resultados exibiram interações entre a fase ativa com as outras fases presentes no intervalo entre 350 - 800 °C, enquanto que a dessorção àtemperatura programada de CO2 (DTP-CO2) mostrou que os catalisadores possuem sítios básicos fracos. Ademais, os catalisadores foram caracterizados por fisissorção de nitrogênio, microscopia eletrônica de varredura (MEV), espectroscopia Raman e basicidade usando um indicador de Hammett. O desempenho dos catalisadores foi avaliado na reação de reforma seca do metano utilizando uma razão molar de alimentação de CH4: CO2 = 1,5:1,0; a fim de simular a composição do biogás. Os resultados mostraram uma maior conversão para o CO2 em todos os catalisadores investigados, o que pode ser atribuído ao maior teor de CH4 alimentado. Além disso, é importante ressaltar a contribuição dos sítios básicos presentes nas amostras, o que pode também contribuir para a conversão do CO2. A maior conversão de CH4 foi observada para os catalisadores tratados a 750 °C. Após as reações, foi observada a formação de carbono grafite sobre todos os catalisadores, com menor percentual para a amostra Ni/ZnAl, calcinadas a 550 °C e 650 °C, e Ni/ZnZr-7, calcinada a 750 °C. Finalmente, os catalisadores calcinados a 650 °C e 750 °C também foram ativados na temperatura de 750°C e os resultados reacionais mostraram que essa temperatura favoreceu o processo de aglomeração e, portanto, promoveu baixas conversões para o CH4 e CO2.

Título en inglés
Evaluation of the performance of catalysts obtained from hydrotalcitas in the dry reform of methane
Palabras clave en inglés
Biogas
Coke
deposition
Dry reforming of methane
Hydrotalcite
Oxide mixture
Syngas
Resumen en inglés

Active and stable catalysts, prepared from the lamellar double hydroxides (HDLs) containing the cations Ni2 +, Zn2 +, Al3 + and Zr4 + (NiZn-Al, NiZn-AlZr and NiZn-Zr) were evaluated in the dry reforming reaction of methane. The precursors were characterized by X-ray diffraction method, confirming the formation of phases for NiZn-Al and NiZn-AlZr samples. Infrared / Raman spectroscopies elucidated the occurrence of anions (CO32-) and water molecules in the interlayer. Nitrogen physisorption (BET method) determined the presence of pores and the specific surface area. The shape of the isotherms were type IV, according to the IUPAC, representing a mesoporous structure. The thermogravimetric analysis was used to determine the calcination temperature of the precursors to obtain the catalysts and the temperatures used were 550 ° C, 650 ° C and 750 ° C. The X-ray diffraction results of the catalysts showed a mixture of binary oxides (NiO, ZnO, ZrO2 and Al2O3) and ternary oxides (NiAl2O4 and ZnAl2O4). The spinel phases were observed in the catalysts obtained at 650 °C (Ni/ZnAl-6 and Ni/ZnAlZr-6) and 750°C (Ni/ZnAl-7 and Ni/ZnAlZr-7) Temperature- programmed reduction with hydrogen (H2-TPR) provided information on catalyst reduction. The results showed interactions between the active phase and the other phases present in the range of 350 - 800 ° C, while temperature- programmed desorption of CO2 (CO2-TPD) showed that the catalysts have weak basic sites. In addition, the catalysts were characterized by Nitrogen physisorption, scanning electron microscopy (SEM), Raman spectroscopy and basicity using a Hammett indicator. The performance of the catalysts was evaluated in the dry reforming reaction of the methane using a CH4: CO2 molar feed ratio = 1.5: 1.0; In order to simulate the biogas composition. The results showed a higher conversion to CO2 in all the catalysts investigated, which can be attributed to the higher content of CH4 fed. In addition, it is important to restate the contribution of the basic sites present in the samples, which may also contribute to the conversion of CO2.The higher conversion of CH4 was observed for the catalysts treated at 750 ° C. After the reactions, the formation of graphite carbon was observed on all the catalysts, with a lower percentage for Ni / ZnAl samples, calcined at 550 ° C and 650 ° C, and Ni / ZnZr-7, calcined at 750 ° C. Finally, the catalysts calcined at 650 ° C and 750 ° C were also activated at the temperature of 750 ° C. and the reaction results showed that this temperature favored the agglomeration process and, therefore, promoted low conversions for CH4 and CO2.

 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-03-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.