Disertación de Maestría
DOI
10.11606/D.75.2009.tde-11032010-111128
Documento
Autor
Nombre completo
Maitê Golinelli Vanella Pedroso
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2009
Director
Tribunal
Plepis, Ana Maria de Guzzi (Presidente)
Parizotto, Nivaldo Antonio
Paula, Marcio de
Título en portugués
Estudo comparativo de colágeno hidrolisado e comercial com adição de PVA
Palabras clave en portugués
Colágeno
PVA
Reologia
Resumen en portugués
O desenvolvimento de novos materiais tem sido baseado na mistura de dois ou mais polímeros ou biopolímeros, onde soluções destes são misturadas em diferentes proporções na tentativa de se obter materiais com propriedades distintas das de seus precursores. Neste trabalho foram analisadas blendas colágeno:PVA. O colágeno utilizado foi o tipo I, porem proveniente de duas formas diferentes, o colágeno comercial que foi cedido pela Novaprom Food Ingredients Ltda e o colágeno obtido a partir de tendão bovino por meio de hidrólise alcalina em diferentes tempos (24h e 96h). As blendas e os colágenos foram caracterizados por análise térmica (DTG e DSC), microscopia eletrônica de varredura (MEV), espectroscopia de absorção no infravermelho (FT-IR) e analises reológicas. As curvas DSC mostraram que o colágeno comercial é o de maior temperatura de desnaturação e que a adição de PVA não altera essa temperatura. Já as curvas TG mostraram que o PVA, seja qual for sua massa molecular, aumenta a estabilidade térmica do colágeno. A microscopia eletrônica mostrou que os colágenos com tratamento alcalino apresentam uma estrutura fibrilar e pouco desorganizada, enquanto o colágeno comercial apresenta uma estrutura uma pouco mais compacta. Através do FT-IR foi possível observar que a presença de PVA nas blendas não influencia na presença dos picos, sugerindo que não há interação química entre os mesmos. A análise reológica permitiu comparar os módulos elástico (G') e viscoso (G") dos géis em diferentes proporções, tendo todos eles valores de G' maior do que G", ou seja, podemos concluir que os materiais são mais elásticos do que viscosos. Observa-se também a influência na viscosidade dos géis com a adição de PVA ao mesmo, sendo a viscosidade maior com o aumento da massa de PVA adicionado.
Título en inglés
Comparative study of commercial and anionic collagen blended with PVA
Palabras clave en inglés
Collagen
PVA
Rheology
Resumen en inglés
The development of new materials has been based on the mix of two or more polymers or biopolymers where solutions are mixed in different portions trying to get materials with distinct properties from their precursors. In this work different collagen solutions and collagen-PVA blends were analyzed. The used collagen was the type I, however obtained from two different forms, the commercial collagen that was provided by Novaprom Food Ingredients Ltda and the collagen obtained from bovine tendon by alkaline hydrolysis in different times (24h and 96h). The blends and collagen were characterized by thermal analysis (DTG and DSC), electronic scan microscopy (ESM), infrared absorption spectroscopy (FT-IR) and rheological analysis. DSC curves showed that the commercial collagen has the highest denaturing temperature and that the addition of PVA does not change this temperature. In other hand, TG curves showed that PVA, in any given molecular weight, increases collagen thermal stability. Electronic microscopy shows that collagen with alkali treatment have a fibrillar and little disorganized structure, insofar, the commercial collagen have a little more compact structure. By FT-IR it was to possible observe that the presence of PVA on blends have no influence on the peaks, suggesting that there is no chemical interaction between then. Rheological analysis allow to compare the elastic module (G') and the viscous module (G'') from blends in different proportions. All the obtained values for G' are higher than G'', so it can be conclude that samples are more elastic than viscous.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-08-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.