Disertación de Maestría
DOI
10.11606/D.75.2007.tde-25102007-165457
Documento
Autor
Nombre completo
Álvaro Fontana
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Motheo, Artur de Jesus (Presidente)
Aoki, Idalina Vieira
Venancio, Everaldo Carlos
Título en portugués
Utilização de polianilina como revestimento protetor contra corrosão das ligas de alumínio 2014 F, 2024 T3 e 7075 O
Palabras clave en portugués
corrosão
eletropolimerização
polianilina
Resumen en portugués
É grande o uso do alumínio em virtude de sua viabilidade técnica e econômica além da alta proteção frente à corrosão conferida pelo filme de óxido de alumínio formado em sua superfície. Neste trabalho foram realizadas deposições de filme de polianilina (PAni) sobre ligas de alumínio AA-2014, AA-2024 e 7075 O. Os experimentos de eletropolimerização foram realizados por voltametria cíclica e cronoamperometria a partir de soluções aquosas contendo ácido fosfórico, ácido sulfâmico e anilina. Para a caracterização dos filmes obtidos sobre as superfícies das ligas foram utilizadas as técnicas de espectroscopia de infravermelho, microscopia eletrônica de varredura e espectroscopia de impedância eletroquímica. Os ensaios de corrosão foram realizados em meio agressivo ao alumínio, solução aquosa de NaCl 0,6 mol L-1 por medidas de polarização potenciodinâmica. Também foi estudada a nucleação dos filmes de PAni por cronoamperometria sobre as mesmas ligas. A partir da caracterização dos polímeros, os resultados demonstram diferenças estruturais entre os filmes de PAni decorrentes do meio ácido utilizado na eletropolimerização, que influencia na proteção contra corrosão. Estruturalmente os filmes eletropolimerizados em meio de ácido fosfórico são mais porosos em relação ao filme de PAni obtido em meio de ácido sulfâmico. Tanto para os filmes obtidos a partir de soluções aquosas de ácido fosfórico como de ácido sulfâmico ocorreram variações estruturais dos filmes após os ensaios de corrosão. Os parâmetros eletroquímicos extraídos das curvas potenciodinâmicas e das análises de impedância demonstram que os filmes obtidos protegem as ligas estudadas contra corrosão. Considerando-se o filme no estado desdopado, para a liga AA-2014, houve um deslocamento no potencial de corrosão de 61,2 mV para valores mais positivos em relação a liga sem recobrimento. Para as outras ligas esse deslocamento foi de 176,1 mV para a liga AA-2024 e 134,3 mV para a liga 7075, evidenciando assim uma maior proteção contra corrosão. Os estudos de corrosão evidenciam que os filmes de PAni podem ser alternativas viáveis aos outros meios protetores utilizados contra corrosão.
Título en inglés
Protection corrosion of aluminum alloys AA-2014 F, AA-2024 T3 and 7075 O by polyaniline
Palabras clave en inglés
corrosion
electropolymerizaton
polyaniline
Resumen en inglés
Aluminum is widely used due to its technical and economic advantages, as well as due to its high level of corrosion protection provided by the oxide film formed on the surface of the metal. In the current study deposition of polyaniline (PAni) on three different Al alloys (AA-2014 F, AA-2024 T3 and 7075 O) was studied. The electrodepositions were realized from aqueous solutions of either phosphoric acid or sulphamic acid that contained the aniline monomer, using the techniques of cyclic voltammetry and chronoamperometry. The films were characterized by infrared spectroscopy (IR), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). To evaluate the resistance of the films under conditions aggressive to Al, potentiodynamic polarization curves were performed in 0,6 mol L-1 NaCl. The nucleation of the films on the aluminum alloys was also investigated using chronoamperometry. Characterization of the PAni films obtained demonstrates that the use of different acids results in distinct structural characteristics, which influence their corrosion protection properties. Structurally the electro-deposited PAni films are more porous when phosphoric acid is used compared to sulphamic acid. After the corrosion assays structural differences are observed, independent of the acid used in the electrosynthesis. Data obtained from the potentioidynamic polarization curves and the impedance measurements indicate that the films obtained protect the alloys studied against corrosion. Considering the film in the undoped form for the alloy AA-2014 F, there was a positive shift in the corrosion potential of 61.2 mV. For the AA-2024 T3 and 7075 O alloys the shifts were 176.1 and 134.4 mV, respectively, indicating a greater degree of corrosion protection. The present study demonstrates that PAni films are viable alternatives to other protection methods.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AlvaroFontana.pdf (21.36 Mbytes)
Fecha de Publicación
2007-10-29
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.