Disertación de Maestría
DOI
10.11606/D.75.2006.tde-16042007-111408
Documento
Autor
Nombre completo
Eurico Yuji Tanabe
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Assaf, Elisabete Moreira (Presidente)
Giudici, Reinaldo
Vielstich, Teresa Benita Iwasita de
Título en portugués
"Óxidos do tipo Perovskitas para reações de decomposição direta de NO e redução de NO com CO"
Palabras clave en portugués
decomposição
NO
Perovskita
Resumen en portugués
Uma tecnologia importante para reduzir a quantidade de poluentes atmosféricos lançados na atmosfera, é a utilização de catalisadores, que convertem os gases altamente poluentes como o NO, para outros gases inofensivos ao meio ambiente. Neste trabalho, os óxidos do tipo perovskitas La2CuO4, LaNiO3, LaMnO3, La1,4Sr0,6CuO4, La0,7Sr0,3NiO3 e La0,7Sr0,3MnO3 foram preparados através do método da co-precipitação, caracterizados por difração de raios-X, redução a temperatura programada, fisissorção de nitrogênio e análise química, e, posteriormente avaliados frente as reações de redução de NO com CO, e decomposição direta de NO. Ambas as reações foram testadas nas temperaturas de 400oC e 500oC e o tempo de reação foi de 7 à 10 horas. Através dos ensaios catalíticos verificou-se que o catalisador La2CuO4 apresentou a maior atividade para a reação de redução, e quando substituiu-se parcialmente o lantânio pelo estrôncio, houve uma melhora significativa para todos os catalisadores. As análises de DRX indicaram que, mesmo após os ensaios catalíticos, a estrutura cristalina dos catalisadores foi preservada.
Título en inglés
"Reduction of NO by CO and direct decomposition of NO on perovskite-type oxide"
Palabras clave en inglés
decomposition
NO
Perovskite
Resumen en inglés
A important technology to reduce the atmospheric pollution is the use of catalysts, to transform high pollutant as NO in other inoffensive gases to the environment. In this work, the perovskite oxides La2CuO4, LaNiO3, LaMnO3, La1,4Sr0,6CuO4, La0,7Sr0,3NiO3 e La0,7Sr0,3MnO3 were prepared through co-precipitation method and characterized by X-ray diffraction and temperature programmed reduction, nitrogen physsisorption and subsequent valued on the reduction of NO by CO and the direct decomposition of NO. These reaction were tested at 400oC and 500oC temperatures and times of reaction between 7 and 10 hours. Through the catalytic tests the La2CuO4 catalyst shown the best activity to the reduce reaction, and when the La is partially substituted by strontium all the catalyst showed a better significant for all the catalysts. The XRD analysis shown that the catalytic structure of the catalysts were preserved after the catalytic test yet.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EuricoYujiTanabe.pdf (1.11 Mbytes)
Fecha de Publicación
2007-04-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.