Mémoire de Maîtrise
DOI
10.11606/D.75.2010.tde-08102010-104357
Document
Auteur
Nom complet
Juliana Ramos de Andrade
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2010
Directeur
Jury
Maule, Agnieszka Joanna Pawlicka (Président)
Huguenin, Fritz Cavalcante
Nogueira, Ana Flavia
Titre en portugais
Eletrólitos poliméricos géis à base de pectina
Mots-clés en portugais
Eletrólitos poliméricos
Impedância
Pectina
Resumé en portugais
Esta dissertação apresenta a preparação e caracterização de eletrólitos poliméricos géis (EPGs) a partir de pectina comercial GENU®, plastificada com glicerol e dopada com perclorato de lítio. O objetivo é a utilização de uma nova matéria-prima para a obtenção de eletrólitos poliméricos substituindo os polímeros sintéticos. A pectina é um polímero natural presente nas plantas; quimicamente é um polímero heterogêneo, e estruturalmente, é constituída unidades repetidas de (1→4)-α-D-ácido galacturônico. Os eletrólitos foram preparados usando como sal LiClO4 (0,24 g ou 30 [O]/[Li]), e 0,6 g de pectina com diferentes quantidades de glicerol (0 g - 2,0 g; 0% - 70%) como plastificante. Os filmes foram caracterizados por espectroscopia de impedância, difração de raios-X, UV-Vis, FT-IR, análises térmicas (DSC e TG). Os melhores resultados foram apresentados pelos filmes constituídos com 70% de glicerol e 30 [O]/[Li] e 68% de glicerol e 0,24 g de LiClO4. .Os filmes com 68% de glicerol apresentam valores de condutividade iônica de 1,61x10-4 S.cm-1 em temperatura ambiente aumentando para 1,72x10-3 S.cm-1 à 80°C, e uma transmitância de 80% no intervalo do visível. Os valores da energia de ativação para este filme é em torno de 37 KJmol-1. Também foi verificada a estabilidade eletroquímica em uma faixa de potencial que varia entre -1,5 a +1,5V. Os filmes com 70% de glicerol apresentam os melhores valores de condutividade iônica de 3,08x10-4 S.cm-1 em temperatura ambiente para 2,94x10-3 S.cm-1 à 80°C, e energia de ativação em torno de 35 KJmol-1, e transmitância de 75% no intervalo do visível. Os resultados obtidos indicaram que os eletrólitos a base de pectina são promissores para aplicações em dispositivos opto-eletroquimicos.
Titre en anglais
Polymer electrolytes gel based on pectin
Mots-clés en anglais
Impedance
Pectin
Polymer electrolytes
Resumé en anglais
This work presents the preparation and characterization of pectin GENU®-based gel polymeric electrolytes (GPEs), plasticized with glycerol and doped with lithium perchlorate. The use of a new raw material for the production of polymeric electrolytes, as substitutes of synthetic polymers is the proposal of this work. Pectin is a natural polymer found in plants. This polymer is chemically heterogeneous and structurally, are composed of a main linear chain of (1→4)-α-D-galacturonic acid. The electrolytes were prepared using salt as LiClO4 (0.24 g or 30 [O]/[Li]) to 0.6 g of pectin and with different amounts of glycerol (0-2.0g, 0-70%) as plasticizer. The films were characterized by impedance spectroscopy, X-ray diffraction, UV-Vis, FT-IR, thermal analysis (DSC and TG). The best results were obtained with films containing 70% of glycerol and 30 [O]/[Li] and 68% of glycerol and 0.24 g LiClO4. The films with 68% of glycerol exhibit ionic conductivity values of 1.61 x10-4 S.cm-1 at room temperature with increase to1.72 x10-3 S.cm-1 at 80°C, and showed a transmittance of 80% in the visible range. The values of activation energy for this sample is around 37 kJmol-1. It was also observed the electrochemical stability in the potential range of -1.5 to +1.5 V. The films with 70% of glycerol showed best ionic conductivity values of 3.08 x10-4 S.cm-1 at room temperature wich increase to 2.94 x10-3 S.cm-1 at 80°C, and activation energy around 35 kJmol-1, and a transmittance of 75% in the visible range. All the obtained results show pectin-based polymer electrolytes over promising materials to be used in opto-electrochemical devices.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2010-12-01
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.