Disertación de Maestría
DOI
10.11606/D.75.2010.tde-08102010-104357
Documento
Autor
Nombre completo
Juliana Ramos de Andrade
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
Maule, Agnieszka Joanna Pawlicka (Presidente)
Huguenin, Fritz Cavalcante
Nogueira, Ana Flavia
Título en portugués
Eletrólitos poliméricos géis à base de pectina
Palabras clave en portugués
Eletrólitos poliméricos
Impedância
Pectina
Resumen en portugués
Esta dissertação apresenta a preparação e caracterização de eletrólitos poliméricos géis (EPGs) a partir de pectina comercial GENU®, plastificada com glicerol e dopada com perclorato de lítio. O objetivo é a utilização de uma nova matéria-prima para a obtenção de eletrólitos poliméricos substituindo os polímeros sintéticos. A pectina é um polímero natural presente nas plantas; quimicamente é um polímero heterogêneo, e estruturalmente, é constituída unidades repetidas de (1→4)-α-D-ácido galacturônico. Os eletrólitos foram preparados usando como sal LiClO4 (0,24 g ou 30 [O]/[Li]), e 0,6 g de pectina com diferentes quantidades de glicerol (0 g - 2,0 g; 0% - 70%) como plastificante. Os filmes foram caracterizados por espectroscopia de impedância, difração de raios-X, UV-Vis, FT-IR, análises térmicas (DSC e TG). Os melhores resultados foram apresentados pelos filmes constituídos com 70% de glicerol e 30 [O]/[Li] e 68% de glicerol e 0,24 g de LiClO4. .Os filmes com 68% de glicerol apresentam valores de condutividade iônica de 1,61x10-4 S.cm-1 em temperatura ambiente aumentando para 1,72x10-3 S.cm-1 à 80°C, e uma transmitância de 80% no intervalo do visível. Os valores da energia de ativação para este filme é em torno de 37 KJmol-1. Também foi verificada a estabilidade eletroquímica em uma faixa de potencial que varia entre -1,5 a +1,5V. Os filmes com 70% de glicerol apresentam os melhores valores de condutividade iônica de 3,08x10-4 S.cm-1 em temperatura ambiente para 2,94x10-3 S.cm-1 à 80°C, e energia de ativação em torno de 35 KJmol-1, e transmitância de 75% no intervalo do visível. Os resultados obtidos indicaram que os eletrólitos a base de pectina são promissores para aplicações em dispositivos opto-eletroquimicos.
Título en inglés
Polymer electrolytes gel based on pectin
Palabras clave en inglés
Impedance
Pectin
Polymer electrolytes
Resumen en inglés
This work presents the preparation and characterization of pectin GENU®-based gel polymeric electrolytes (GPEs), plasticized with glycerol and doped with lithium perchlorate. The use of a new raw material for the production of polymeric electrolytes, as substitutes of synthetic polymers is the proposal of this work. Pectin is a natural polymer found in plants. This polymer is chemically heterogeneous and structurally, are composed of a main linear chain of (1→4)-α-D-galacturonic acid. The electrolytes were prepared using salt as LiClO4 (0.24 g or 30 [O]/[Li]) to 0.6 g of pectin and with different amounts of glycerol (0-2.0g, 0-70%) as plasticizer. The films were characterized by impedance spectroscopy, X-ray diffraction, UV-Vis, FT-IR, thermal analysis (DSC and TG). The best results were obtained with films containing 70% of glycerol and 30 [O]/[Li] and 68% of glycerol and 0.24 g LiClO4. The films with 68% of glycerol exhibit ionic conductivity values of 1.61 x10-4 S.cm-1 at room temperature with increase to1.72 x10-3 S.cm-1 at 80°C, and showed a transmittance of 80% in the visible range. The values of activation energy for this sample is around 37 kJmol-1. It was also observed the electrochemical stability in the potential range of -1.5 to +1.5 V. The films with 70% of glycerol showed best ionic conductivity values of 3.08 x10-4 S.cm-1 at room temperature wich increase to 2.94 x10-3 S.cm-1 at 80°C, and activation energy around 35 kJmol-1, and a transmittance of 75% in the visible range. All the obtained results show pectin-based polymer electrolytes over promising materials to be used in opto-electrochemical devices.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-12-01
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.