Disertación de Maestría
DOI
10.11606/D.75.2006.tde-04062007-105547
Documento
Autor
Nombre completo
Rudye Kleber da Silva Santos
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2006
Director
Tribunal
Assaf, Elisabete Moreira (Presidente)
Assaf, José Mansur
Florentino, Ariovaldo de Oliveira
Título en portugués
"Caracterização e aplicação de catalisadores de cobalto suportados em g-Al2O3 e SiO2 para produção de hidrogênio a partir da reforma a vapor e oxidativa de etanol"
Palabras clave en portugués
catalisador de cobalto
produção de hidrogênio
reforma a vapor de etanol
reforma oxidativa de etanol
Resumen en portugués
Neste trabalho foram preparados catalisadores Co/Al2O3 e Co/SiO2 por impregnação com concentração metálica entre 4,0% e 20,0% e avaliados frente às reações de reforma a vapor e reforma oxidativa de etanol, com o objetivo de avaliar a estabilidade catalítica e o rendimento em hidrogênio. Os catalisadores foram caracterizados por espectrofotometria de absorção atômica, difração de raios-X, espectroscopia Raman, redução a temperatura programada, fisissorção de nitrogênio e análise elementar de carbono. A caracterização das amostras mostrou a formação da fase Co3O4 e interações de espécies de cobalto com o suporte. Evidenciou-se que apenas os sítios de Co0 são ativos para as reações de reforma a vapor e oxidativa de etanol. A produção de hidrogênio variou de 50-70% e a de CO de 0-10%. Alta concentração metálica sobre a superfície do suporte acarretou uma baixa produção de monóxido de carbono. As reações tiveram deposições de carbono nos catalisadores variando de 2,7 a 12,7 (mg. h-1), indicando que a desativação dos materiais é devido a deposição de coque. O uso de oxigênio diminuiu a produção de coque sobre os catalisadores Co/Al2O3 e Co/SiO2.
Título en inglés
"Characterization and application of cobalt catalyst supported on g-Al2O3 e SiO2 for the production of hidrogen from the ethanol steam and oxidative reforming"
Palabras clave en inglés
cobalt catalyst
ethanol oxidative reforming
ethanol steam reforming
hydrogen production
Resumen en inglés
In this work Co/Al2O3 and Co/SiO2 catalysts were prepared by impregnation with metal load between 4,0% and 20,0% and were evaluated in the reactions of ethanol steam reforming and ethanol oxidative reforming to study the catalytic stability and the hydrogen yield. Atomic absorption, X-ray powder diffraction, Raman spectroscopy, temperature programmed reduction, nitrogen fisisorption and elemental analysis of carbon were applied to describe the physical and chemical characteristics of these catalysts. The characterization of the catalysts showed the Co3O4 phase and interactions of cobalt species with the support. It was evidenced that only Co0 sites are active for the steam reforming and oxidative reforming of ethanol. The production of hydrogen was about 50-70% and CO was 0- 10%. A high metallic load gave less carbon monoxide production. In the reactions, 2,7-12,7(mg.h-1) of carbon was deposited on all catalysts, indicating that the deactivation of the materials is due to coke deposition. The use of oxygen decreases the production of carbon on the catalysts Co/Al2O3 and Co/SiO2.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
RudyeKSSantos.pdf (719.18 Kbytes)
Fecha de Publicación
2007-06-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.