Tesis Doctoral
DOI
10.11606/T.74.2017.tde-22112017-165352
Documento
Autor
Nombre completo
André Diniz Rosa da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Pirassununga, 2017
Director
Tribunal
Pallone, Eliria Maria de Jesus Agnolon (Presidente)
Godoi, Ana Paula Terossi de
Osiro, Denise
Pierri, Juliano de
Tonin, Fernando Gustavo
Título en portugués
Obtenção de cerâmicas porosas de alumina-zircônia pelo método da réplica recobertas com fosfato de cálcio
Palabras clave en portugués
Alumina-zircônia
Fosfato de cálcio
Método da réplica
Recobrimento biomimético
Scaffolds
Resumen en portugués
As cerâmicas porosas empregadas na substituição óssea, são utilizadas por apresentarem características como biocompatibilidade, ter estrutura tridimensional e apresentar alta porosidade. Nesse sentido, o objetivo desse trabalho foi obter e caracterizar cerâmicas porosas de Al2O3 e Al2O3 contendo 5% em volume de inclusões de ZrO2, produzidas pelo método da réplica. Essas cerâmicas porosas tiveram sua superfície tratada quimicamente com ácido fosfórico e foram recobertos, com fosfato de cálcio usando o método biomimético, em solução de SBF 5X (Simulated Body Fluid) por um período de incubação de 14 dias. Após o recobrimento, algumas cerâmicas porosas foram tratadas quimicamente para incorporação do Sr2+. Em seguida foram caracterizadas morfologicamente e estruturalmente usando ensaios de compressão axial, porosidade aparente, microscopia eletrônica de varredura (MEV), microtomografia de Raio X (µ-CT), difratometria de Raio X (DRX), Espectroscopia de Infravermelho Próximo (NIR), emissão óptica com plasma indutivamente acoplado (ICP-OES), Energia Dispersiva de Raio-X (EDS) e por Ensaios biológicos utilizando cultura de células para análise de viabilidade celular. As cerâmicas porosas de alumina e alumina-zircônia apresentaram, respectivamente, porosidade aparente de 80,93 % e 78,82 %, resistência à compressão axial, 2,93 MPa e 6,59 MPa, além de uma ampla faixa de tamanho de poros de, desejáveis para o favorecimento de interesses biológicos destinados à regeneração e formação de tecido ósseo. O recobrimento biomimético usando SBF 5X produziu a formação das fases α-TCP, β-TCP, TTCP e Hidroxiapatita, usando período de incubação de 14 dias. A incorporação de Sr2+ na estrutura dos fosfatos mostrou-se mais eficientes nos corpos porosos de alumina-zircônia. Os ensaios in vitro mostraram a biocompatibilidade das cerâmicas porosas estudadas, demonstrando a possibilidade de sua utilização como material para substituição ou preenchimento ósseo.
Título en inglés
Obtaining porous alumina-zirconia ceramics by the calcium phosphate-coated replica method
Palabras clave en inglés
Alumina-zirconia
Biomimetic coating
Calcium phosphate
Replica method
Scaffolds
Resumen en inglés
The porous ceramics used in bone substitution are used because they present characteristics as biocompatibility, have a three - dimensional structure and have high porosity. In this sense, the objective of this work was to obtain and characterize porous ceramics of Al2O3 and Al2O3 containing 5% by volume of ZrO2 inclusions, produced by the replica method. These porous ceramics were chemically treated with phosphoric acid and were coated with calcium phosphate using the biomimetic method in 5X SBF solution (Simulated Body Fluid) for a 14 day incubation period. After coating, some porous ceramics were chemically treated for Sr2+ incorporation. They were then characterized morphologically and structurally using axial compression, apparent porosity, scanning electron microscopy (SEM), microtomography (µ-CT), X-ray diffractometry (XRD), Near Infrared (NIR) Coupled (ICP-OES), X-ray Dispersive Energy (EDS) and Biological Assays using cell culture for cell viability analysis. The porous ceramics of alumina and alumina-zirconia showed, respectively, 80.93% and 78.82% apparent porosity, axial compression strength, 2.93 MPa and 6.59 MPa, as well as a wide range of pore size, desirable for the promotion of biological interests destined to the regeneration and formation of bone tissue. Biomimetic coated using SBF 5X produced the formation of α-TCP, β-TCP, TTCP and Hydroxyapatite phases using a 14-day incubation period. The incorporation of Sr2+ in the phosphate structure proved to be more efficient in porous alumina-zirconia bodies. The in vitro tests showed the biocompatibility of the porous ceramics studied, demonstrating the possibility of their use as material for bone replacement or filling.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DO5576440COR.pdf (4.07 Mbytes)
Fecha de Publicación
2017-12-01
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.