Doctoral Thesis
DOI
https://doi.org/10.11606/T.74.2017.tde-22112017-165352
Document
Author
Full name
André Diniz Rosa da Silva
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Pirassununga, 2017
Supervisor
Committee
Pallone, Eliria Maria de Jesus Agnolon (President)
Godoi, Ana Paula Terossi de
Osiro, Denise
Pierri, Juliano de
Tonin, Fernando Gustavo
Title in Portuguese
Obtenção de cerâmicas porosas de alumina-zircônia pelo método da réplica recobertas com fosfato de cálcio
Keywords in Portuguese
Alumina-zircônia
Fosfato de cálcio
Método da réplica
Recobrimento biomimético
Scaffolds
Abstract in Portuguese
As cerâmicas porosas empregadas na substituição óssea, são utilizadas por apresentarem características como biocompatibilidade, ter estrutura tridimensional e apresentar alta porosidade. Nesse sentido, o objetivo desse trabalho foi obter e caracterizar cerâmicas porosas de Al2O3 e Al2O3 contendo 5% em volume de inclusões de ZrO2, produzidas pelo método da réplica. Essas cerâmicas porosas tiveram sua superfície tratada quimicamente com ácido fosfórico e foram recobertos, com fosfato de cálcio usando o método biomimético, em solução de SBF 5X (Simulated Body Fluid) por um período de incubação de 14 dias. Após o recobrimento, algumas cerâmicas porosas foram tratadas quimicamente para incorporação do Sr2+. Em seguida foram caracterizadas morfologicamente e estruturalmente usando ensaios de compressão axial, porosidade aparente, microscopia eletrônica de varredura (MEV), microtomografia de Raio X (µ-CT), difratometria de Raio X (DRX), Espectroscopia de Infravermelho Próximo (NIR), emissão óptica com plasma indutivamente acoplado (ICP-OES), Energia Dispersiva de Raio-X (EDS) e por Ensaios biológicos utilizando cultura de células para análise de viabilidade celular. As cerâmicas porosas de alumina e alumina-zircônia apresentaram, respectivamente, porosidade aparente de 80,93 % e 78,82 %, resistência à compressão axial, 2,93 MPa e 6,59 MPa, além de uma ampla faixa de tamanho de poros de, desejáveis para o favorecimento de interesses biológicos destinados à regeneração e formação de tecido ósseo. O recobrimento biomimético usando SBF 5X produziu a formação das fases α-TCP, β-TCP, TTCP e Hidroxiapatita, usando período de incubação de 14 dias. A incorporação de Sr2+ na estrutura dos fosfatos mostrou-se mais eficientes nos corpos porosos de alumina-zircônia. Os ensaios in vitro mostraram a biocompatibilidade das cerâmicas porosas estudadas, demonstrando a possibilidade de sua utilização como material para substituição ou preenchimento ósseo.
Title in English
Obtaining porous alumina-zirconia ceramics by the calcium phosphate-coated replica method
Keywords in English
Alumina-zirconia
Biomimetic coating
Calcium phosphate
Replica method
Scaffolds
Abstract in English
The porous ceramics used in bone substitution are used because they present characteristics as biocompatibility, have a three - dimensional structure and have high porosity. In this sense, the objective of this work was to obtain and characterize porous ceramics of Al2O3 and Al2O3 containing 5% by volume of ZrO2 inclusions, produced by the replica method. These porous ceramics were chemically treated with phosphoric acid and were coated with calcium phosphate using the biomimetic method in 5X SBF solution (Simulated Body Fluid) for a 14 day incubation period. After coating, some porous ceramics were chemically treated for Sr2+ incorporation. They were then characterized morphologically and structurally using axial compression, apparent porosity, scanning electron microscopy (SEM), microtomography (µ-CT), X-ray diffractometry (XRD), Near Infrared (NIR) Coupled (ICP-OES), X-ray Dispersive Energy (EDS) and Biological Assays using cell culture for cell viability analysis. The porous ceramics of alumina and alumina-zirconia showed, respectively, 80.93% and 78.82% apparent porosity, axial compression strength, 2.93 MPa and 6.59 MPa, as well as a wide range of pore size, desirable for the promotion of biological interests destined to the regeneration and formation of bone tissue. Biomimetic coated using SBF 5X produced the formation of α-TCP, β-TCP, TTCP and Hydroxyapatite phases using a 14-day incubation period. The incorporation of Sr2+ in the phosphate structure proved to be more efficient in porous alumina-zirconia bodies. The in vitro tests showed the biocompatibility of the porous ceramics studied, demonstrating the possibility of their use as material for bone replacement or filling.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
DO5576440COR.pdf (4.07 Mbytes)
Publishing Date
2017-12-01
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.